PC PANLITE® LN-2250Y TEIJIN JAPAN
287
- Unit Price:US$ 5,026 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:38.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜optical performance
- Application Areas:Optical level
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D-542 | 1585 | |
| transmittance | ASTM D-1003 | 88 % | |
| melt mass-flow rate | ISO 1133 | 11.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| ISO 294-4 | 0.50-0.70 % | ||
| Water absorption rate | ISO 62 | 0.20 % |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 本公司制订的测定法 | 0.5-0.7 % | |
| 本公司制订的测定法 | 0.5-0.7 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | ASTM D1003/ISO 13468 | 88 % | |
| refractive index | ASTM D542/ISO 489 | 1.585 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 6.00mm | |
| UL -94 | V-2 0.43mm | ||
| UL -94 | V-0 3.00mm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1200 kg/m | |
| Water absorption rate | ASTM D-570 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ISO 527-1 and ISO 527-2 | >50 % | |
| Impact strength of cantilever beam gap | ISO 179 | NB KJ/m | |
| Tensile modulus | ISO 527-1 and ISO 527-2 | 2400 Mpa | |
| Impact strength of cantilever beam gap | ISO 179 | 12 KJ/m | |
| bending strength | ISO 178 | 92 Mpa | |
| Tensile stress | ISO 527-1 and ISO 527-2 | 61 Mpa | |
| elongation at yield | ISO 527-1 and ISO 527-2 | 6 % | |
| Flexural modulus | ISO 178 | 2350 Mpa | |
| tensile strength | ISO 527-2 | 61.0 Mpa | |
| elongation at break | ISO 527-2 | 6.0 % | |
| ISO 527-2 | >50 % | ||
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| bending strength | ISO 178 | 92.0 Mpa | |
| Flexural modulus | ISO 178 | 2350 Mpa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 76 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | NB kJ/m² | |
| Tensile modulus | ASTM D638/ISO 527 | /2400 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | /61 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | /6 % | |
| Flexural modulus | ASTM D790/ISO 178 | /2350 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | /92 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric loss | IEC 60250 | 90 | |
| dielectric constant | IEC 60250 | 3.1 | |
| Surface Resistivity | IEC 600 | >1×10 Ω | |
| arc resistance | IEC 60112 | 225 | |
| dielectric strength | IEC 60243-1 | 32 MV/m | |
| Volume resistivity | IEC 60093 | >1×10 Ω.cm | |
| Dielectric loss | IEC 60250 | 10 | |
| dielectric constant | IEC 60250 | 3 | |
| Volume resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm | |
| dielectric constant | IEC 60250 | 32 1kHz | |
| IEC 60250 | 3.00 1MHz | ||
| IEC 60250 | 3.10 100HZ | ||
| Dissipation Factor | IEC 60250 | 1E-03 | |
| IEC 60250 | 9E-03 | ||
| IEC 60112 | 225 V | ||
| dielectric constant | ASTM D150/IEC 60250 | 3.1 | |
| ASTM D150/IEC 60250 | 3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | /1200 | |
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 308 | 148 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.7 | |
| ISO 11359-2 | 0.7 | ||
| Heat distortion temperature | ISO 75-1 and ISO 75-2 | 141 °C | |
| TEMPERATURE | UL 746B | 125 °C | |
| UL 746B | 115 °C | ||
| UL 746B | 125 °C | ||
| Heat distortion temperature | ISO 75-1 and ISO 75-2 | 128 °C | |
| ISO 75-2/Bf | 141 °C | ||
| ISO 75-2/A | 128 °C | ||
| vicat | ISO 306/B50 | 148 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 7E-05 cm/cm/°C | |
| ISO 11359-2 | 7E-05 cm/cm/°C | ||
| vicat | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.