PC Makrolon®  2865 COVESTRO GERMANY

244
  • Unit Price:US$ 2,168 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    50MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Medium viscosity｜transparent
  • Application Areas:Electrical field｜Electronic field｜Automotive sector｜Household appliances｜Household appliances
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
turbidity3000μmISO 14782<0.80 %
transmissivity4000μmISO 13468-287.0 %
transmissivity3000μmISO 13468-288.0 %
transmissivity2000μmISO 13468-289.0 %
Refractive indexISO 4891.586
transmissivity1000μmISO 13468-289.0 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°C,Partial BreakISO 739175 kJ/m²
Charpy Notched Impact Strength-30°C,Complete BreakISO 739116 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739112 kJ/m²
Impact strength of cantilever beam gap23°C,Partial BreakISO 739165 kJ/m²
Multi axis Instrumented Peak Impact Force23°CISO 6603-25400 N
Multi axis Instrumented Impact Energy-30°CISO 6603-265.0 J
Multi axis Instrumented Impact Energy23°CISO 6603-260.0 J
Multi axis Instrumented Peak Impact Force-30°CISO 6603-26300 N
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating6.0mmUL 94V-0
Hot filament ignition temperature1.5mmIEC 60695-2-13900 °C
Burning wire flammability index0.75mmIEC 60695-2-12850 °C
Burning wire flammability index1.5mmIEC 60695-2-12850 °C
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.75mmIEC 60695-2-13875 °C
UL flame retardant rating0.75mmUL 94V-2
FlashIgnitionTemperatureASTM D1929480 °C
Needle flame testMethodF:1.50mmIEC 60695-11-51.0 min
Hot filament ignition temperature3.0mmIEC 60695-2-13900 °C
Extreme Oxygen IndexISO 4589-232 %
ApplicationofFlamefromSmallBurner MethodKandF2.00mmDIN 53438-1,-3K1.F1
Burning rate - US-FMVSS>1.00mmISO 3795passed
Needle flame testMethodF:2.00mmIEC 60695-11-52.0 min
Needle flame testMethodF:3.00mmIEC 60695-11-52.0 min
Needle flame testMethodK:1.50mmIEC 60695-11-50.2 min
Needle flame testMethodK:2.00mmIEC 60695-11-50.3 min
Needle flame testMethodK:3.00mmIEC 60695-11-50.5 min
SelfIgnitionASTM D1929550 °C
mechanical propertiesTest ConditionTest MethodTest Result
Bending strain23°CISO 1787.1 %
bending strength23°CISO 17897.0 Mpa
bending strength3.5%Strain,23°CISO 17873.0 Mpa
Bending modulus23°CISO 1782400 Mpa
Tensile creep modulus1000hrISO 899-11900 Mpa
Tensile creep modulus1hrISO 899-12200 Mpa
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Tensile strainBreak,23°CISO 527-2/50130 %
Tensile strainYield,23°CISO 527-2/506.2 %
Tensile modulus23°CISO 527-2/12400 Mpa
tensile strengthYield,23°CISO 527-2/5066.0 Mpa
tensile strengthBreak,23°CISO 527-2/5070.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B137 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A125 °C
Glass transition temperatureISO 11357-2145 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120146 °C
Ball Pressure Test136°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
thermal conductivity23°CISO 83020.20 W/m/K
RTI Elec1.5mmUL 746125 °C
RTI Imp1.5mmUL 746115 °C
RTI Str1.5mmUL 746125 °C
Physical propertiesTest ConditionTest MethodTest Result
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113310.0 cm3/10min
Shrinkage rateTDISO 25770.60-0.80 %
Shrinkage rateMDISO 25770.60-0.80 %
Shrinkage rateTD:2.00mm3ISO 294-40.70 %
Shrinkage rateMD:2.00mm3ISO 294-40.65 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
density23°CISO 11831.20 g/cm³
Apparent densityISO 600.64 g/cm³
melt mass-flow rate300°C/1.2kgISO 113310 g/10min
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931E+16 ohms
Compared to the anti leakage trace indexSolutionBIEC 60112PLC 4
Volume resistivity23°CIEC 600931E+16 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-134 KV/mm
Relative permittivity23°C,100HzIEC 602503.10
Relative permittivity23°C,1MHzIEC 602503.00
Dissipation factor23°C,100HzIEC 602505E-04
Dissipation factor23°C,1MHzIEC 602509E-03
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 3
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1115 Mpa
filmTest ConditionTest MethodTest Result
GasPermeationOxygen:23°C,100.0μmISO 2556650 cm³/m²/bar/24hr
GasPermeationOxygen:23°C,25.4μmISO 25562760 cm³/m²/bar/24hr
GasPermeationNitrogen:23°C,100.0μmISO 2556120 cm³/m²/bar/24hr
GasPermeationNitrogen:23°C,25.4μmISO 2556510 cm³/m²/bar/24hr
GasPermeationCarbonDioxide:23°C,100.0μmISO 25563800 cm³/m²/bar/24hr
GasPermeationCarbonDioxide:23°C,25.4μmISO 255616900 cm³/m²/bar/24hr
Water vapor permeability23°C,85%RH,100μmISO 15106-115 g/m²/24hr
Supplementary InformationTest ConditionTest MethodTest Result
Electrolytic corrosion23°CIEC 60426A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.