PA6 AKROMID® B3 GF 30 AKRO-PLASTIC GERMANY

405

Unit Price:US$ 2,414 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength｜High rigidity｜Glass fiber reinforced｜enhance｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Engineering accessories｜Automotive sector｜engineering application ｜engineering application
Color:--
Grade:Wear resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	FMVSS302	<100 mm/min
UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	1.6mm	IEC 60695-2-12	650 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	10300 Mpa
tensile strength	Break	ISO 527-2/5	185 Mpa
Tensile strain	Break	ISO 527-2/5	3.0 %
Bending modulus		ISO 178	8500 Mpa
bending strength		ISO 178	270 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	210 °C
Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	150 °C
Melting temperature		DIN EN11357-1	220 °C
Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	1.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	9.5E-05 cm/cm/°C
TemperatureIndex	50%LossofTensileStrength,20000hr	IEC 216	130to150 °C
TemperatureIndex	TemperatureIndex	50%LossofTensileStrength,5000hr	IEC 216	160to175 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Test Condition	Test Method	Test Result
Spiral flow length		Internal Method	66.0 CM
Shrinkage rate	TD	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.10 %
Water absorption rate	Saturation,23°C	ISO 62	6.3to6.9 %
Hygroscopicity	70°C，62%RH	ISO 1110	2.1to2.3 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+12 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
Compared to the anti leakage trace index	SolutionA	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H961/30	ISO 2039-1	230 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
ReinforcementContent		ISO 1172	30 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 AKROMID® B3 GF 30 AKRO-PLASTIC GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet