impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	V-0
Flammability level	Flammability level		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	245	Mpa
Bending modulus		ISO 178	11500	Mpa
tensile strength	Break	ISO 527-2	155	Mpa
Tensile modulus	160°C	ISO 527-2	5000	Mpa
	Tensile modulus	120°C	ISO 527-2	7500	Mpa
	Tensile modulus	Tensile modulus	--	ISO 527-2	12000	Mpa
Tensile strain	Break, 160°C	ISO 527-2	3.7	%
	Tensile strain	Break, 120°C	ISO 527-2	2.7	%
	Tensile strain	Tensile strain	Break	ISO 527-2	2.0	%
tensile strength	Break, 160°C	ISO 527-2	70.0	Mpa
tensile strength	tensile strength	Break, 120°C	ISO 527-2	100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Thermal Index - 5000 hr		IEC 60216	163	°C
RTI Elec	0.35 mm	UL 746	140	°C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	3.5E-5 7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5 3.0E-5	cm/cm/°C
Melting temperature		ISO 11357-3	325	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	305	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.6	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1 MHz	IEC 60250	3.90
	Relative permittivity	1.00 GHz	IEC 60250	3.90
	Relative permittivity	Relative permittivity	100 Hz	IEC 60250	4.20
Dielectric strength		IEC 60243-1	33	KV/mm
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Relative permittivity	10.0 GHz	IEC 60250	3.90
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.