PC/ABS

PC/ABS INFINO® NH-1000T Samsung Cheil South Korea

340

Unit Price:US$ 3,664 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:OA device｜Mechanical accessories｜Casters
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	35 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	390 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	39 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-1
		UL flame retardant rating	2.0mm	UL 94	V-0
			UL flame retardant rating	3.0mm	UL 94	V-0
			UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	77.0 Mpa
Bending modulus		ISO 178	2700 Mpa
Bending modulus	Bending modulus		ASTM D790	2400 Mpa
Tensile strain	Break	ISO 527-2/50	78 %
tensile strength	Break	ISO 527-2/50	44.0 Mpa
	tensile strength	Yield	ISO 527-2/50	54.0 Mpa
	tensile strength	tensile strength	Yield	ASTM D638	54.0 Mpa
Tensile modulus		ISO 527-2/50	2500 Mpa
bending strength		ISO 178	81.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B120	91.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	89.0 °C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	84.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	76.0 °C
		Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	92.0 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	86.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.17 g/cm³
density	density		ASTM D792	1.17 g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	39 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	39 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	114
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS INFINO® NH-1000T Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet