PC Makrolon® 8035 000000 COVESTRO GERMANY
194
- Unit Price:US$ 3,763 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜enhance｜Filler: Glass fiber with embossing｜30%｜Filler by weight｜30% filler by weight
- Application Areas:Electrical field｜Electronic field｜Fiber grade
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.42 g/cm³ | |
| Apparent density | ISO 60 | 0.69 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 5.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 4.00 cm3/10min | |
| Shrinkage rate | ISO 2577 | 0.25-0.40 % | |
| ISO 2577 | 0.25-0.40 % | ||
| ISO 294-4 | 0.35 % | ||
| ISO 294-4 | 0.50 % | ||
| Water absorption rate | ISO 62 | 0.22 % | |
| ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 149 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| needle flame test | IEC 60695-11-5 | 2.0 min | |
| IEC 60695-11-5 | 2.0 min | ||
| IEC 60695-11-5 | 2.0 min | ||
| IEC 60695-11-5 | 1.0 min | ||
| IEC 60695-11-5 | 1.0 min | ||
| IEC 60695-11-5 | 2.0 min | ||
| SelfIgnitionTemperature | ASTM D1929 | 550 °C | |
| UL flame retardant rating | UL 94 | V-1 | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C | ||
| IEC 60695-2-13 | 875 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 37 % | |
| ApplicationofFlamefromSmallBurner-Method | DIN 53438-1,-3 | K1.F1 | |
| Burning rate - US-FMVSS | ISO 3795 | passed | |
| FlashIgnitionTemperature | ASTM D1929 | 470 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| electrolytic corrosion | IEC 60426 | A1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/5 | 55.0 Mpa | |
| Tensile strain | ISO 527-2/50 | 2.5 % | |
| ISO 527-2/5 | 3.5 % | ||
| Tensile creep modulus | ISO 899-1 | 4700 Mpa | |
| ISO 899-1 | 3900 Mpa | ||
| Flexural modulus | ISO 178 | 4700 Mpa | |
| bending strength | ISO 178 | 100 Mpa | |
| ISO 178 | 105 Mpa | ||
| Bending Strain | ISO 178 | 4.5 % | |
| Tensile modulus | ISO 527-2/1 | 5100 Mpa | |
| tensile strength | ISO 527-2/50 | 59.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 7391 | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 45 kJ/m² | |
| ISO 179/1eU | 45 kJ/m² | ||
| ISO 179/1eU | 40 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 7391 | 8.0 kJ/m² | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 5.00 J | |
| ISO 6603-2 | 5.00 J | ||
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 800 N | |
| ISO 6603-2 | 1300 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| relative permittivity | IEC 60250 | 3.50 | |
| IEC 60250 | 3.50 | ||
| Dissipation Factor | IEC 60250 | 1.5E-03 | |
| IEC 60250 | 9E-03 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| IEC 60112 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 141 °C | |
| ISO 75-2/A | 135 °C | ||
| vicat | ISO 306/B50 | 147 °C | |
| ISO 306/B120 | 148 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 3.5E-05 cm/cm/°C | |
| ISO 11359-2 | 5.5E-05 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.24 W/m/K | |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI Str | UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.