Plastic Raw Materials
PC

PC 2205 751636 COVESTRO SHANGHAI

231
  • Unit Price:US$ 2,795 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low viscosity｜Easy to demould
  • Application Areas:currency
  • Color:--
  • Grade:High liquidity level

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexISO 4891.586
transmissivity1000μmISO 13468-289.0 %
transmissivity2000μmISO 13468-289.0 %
transmissivity3000μmISO 13468-288.0 %
transmissivity4000μmISO 13468-287.0 %
turbidity3000μmISO 14782<0.80 %
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°C,Complete BreakISO 739112 kJ/m²
Charpy Notched Impact Strength23°C,Partial BreakISO 739155 kJ/m²
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739112 kJ/m²
Impact strength of cantilever beam gap23°C,Partial BreakISO 739155 kJ/m²
Multi axis Instrumented Impact Energy-30°CISO 6603-260.0 J
Multi axis Instrumented Impact Energy23°CISO 6603-255.0 J
Multi axis Instrumented Peak Impact Force-30°CISO 6603-25900 N
Multi axis Instrumented Peak Impact Force23°CISO 6603-24900 N
flammabilityTest ConditionTest MethodTest Result
Needle flame testMethodK:2.00mmIEC 60695-11-50.1 min
Needle flame testMethodK:1.50mmIEC 60695-11-50.1 min
Needle flame testMethodF:3.00mmIEC 60695-11-52.0 min
Needle flame testMethodF:2.00mmIEC 60695-11-52.0 min
Needle flame testMethodF:1.50mmIEC 60695-11-51.0 min
FlashIgnitionTemperatureASTM D1929480 °C
Burning rate - US-FMVSS>1.00mmISO 3795passed
ApplicationofFlamefromSmallBurner MethodKandF2.00mmDIN 53438-1,-3K1.F1
Extreme Oxygen IndexISO 4589-228 %
Hot filament ignition temperature3.0mmIEC 60695-2-13875 °C
Needle flame testMethodK:3.00mmIEC 60695-11-50.2 min
SelfIgnitionASTM D1929550 °C
UL flame retardant rating2.9mmUL 94HB
UL flame retardant rating0.75mmUL 94V-2
Burning wire flammability index0.75mmIEC 60695-2-12850 °C
Burning wire flammability index1.5mmIEC 60695-2-12875 °C
Burning wire flammability index3.0mmIEC 60695-2-12930 °C
Hot filament ignition temperature0.75mmIEC 60695-2-13875 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13875 °C
Hot filament ignition temperature1.5mmIEC 60695-2-13875 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainBreak,23°CISO 527-2/50120 %
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Tensile creep modulus1hrISO 899-12100 Mpa
Tensile creep modulus1000hrISO 899-11700 Mpa
Tensile strainYield,23°CISO 527-2/506.0 %
tensile strengthBreak,23°CISO 527-2/5060.0 Mpa
tensile strengthYield,23°CISO 527-2/5065.0 Mpa
Tensile modulus23°CISO 527-2/12400 Mpa
Bending strain23°CISO 1787.1 %
bending strength23°CISO 17897.0 Mpa
Bending modulus23°CISO 1782350 Mpa
bending strength3.5%Strain,23°CISO 17873.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120146 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B137 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A124 °C
Glass transition temperatureISO 11357-2145 °C
Ball Pressure Test136°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
thermal conductivity23°CISO 83020.20 W/m/K
RTI Imp1.5mmUL 746115 °C
RTI Str1.5mmUL 746125 °C
RTI Elec1.5mmUL 746125 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTDISO 25770.50-0.70 %
Shrinkage rateMDISO 25770.50-0.70 %
density23°CISO 11831.19 g/cm³
Apparent densityISO 600.66 g/cm³
melt mass-flow rate300°C/1.2kgISO 113337 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113334.0 cm3/10min
Shrinkage rateTD:2.00mm3ISO 294-40.65 %
Shrinkage rateMD:2.00mm3ISO 294-40.65 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 2
Compared to the anti leakage trace indexSolutionBIEC 60112PLC 4
Surface resistivityIEC 600931E+16 ohms
Volume resistivity23°CIEC 600931E+16 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-134 KV/mm
Relative permittivity23°C,100HzIEC 602503.10
Relative permittivity23°C,1MHzIEC 602503.00
Dissipation factor23°C,100HzIEC 602505E-04
Dissipation factor23°C,1MHzIEC 602509E-03
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1115 Mpa
filmTest ConditionTest MethodTest Result
GasPermeationOxygen:23°C,100.0μmISO 2556750 cm³/m²/bar/24hr
GasPermeationOxygen:23°C,25.4μmISO 25563150 cm³/m²/bar/24hr
GasPermeationNitrogen:23°C,100.0μmISO 2556150 cm³/m²/bar/24hr
GasPermeationNitrogen:23°C,25.4μmISO 2556630 cm³/m²/bar/24hr
GasPermeationCarbonDioxide:23°C,100.0μmISO 25564500 cm³/m²/bar/24hr
GasPermeationCarbonDioxide:23°C,25.4μmISO 255618900 cm³/m²/bar/24hr
Water vapor permeability23°C,85%RH,100μmISO 15106-115 g/m²/24hr
Supplementary InformationTest ConditionTest MethodTest Result
Electrolytic corrosion23°CIEC 60426A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.