PA6 Durethan® AKV30H1.0-NC LANXESS GERMANY
175
- Unit Price:US$ 3,336 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:113MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.060 % | |
| Water absorption rate | ISO 62 | 5.5 % | |
| ISO 62 | 2.0 % | ||
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.94 % | |
| ISO 294-4 | 0.12 % | ||
| ISO 294-4 | 0.44 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 205 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| Burning wire flammability index | IEC 60695-2-12 | 650 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| Burning Behavior | ISO 3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA66.GHWR.14-100.GF30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 9430 Mpa | |
| ISO 527-2/1 | 9700 Mpa | ||
| tensile strength | ASTM D638 | 175 Mpa | |
| ISO 527-2/5 | 180 Mpa | ||
| elongation | ASTM D638 | 4.0 % | |
| Tensile strain | ISO 527-2/5 | 3.5 % | |
| Flexural modulus | ASTM D790 | 8620 Mpa | |
| ISO 178/A | 8600 Mpa | ||
| bending strength | ASTM D790 | 281 Mpa | |
| ISO 178/A | 265 Mpa | ||
| ISO 178 | 280 Mpa | ||
| 4.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 65 kJ/m² | |
| ISO 179/1eU | 75 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 60 kJ/m² | |
| ISO 180/1U | 70 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thin film puncture strength | ISO 6603-2 | 3.10 J | |
| ISO 6603-2 | 1.90 J | ||
| ISO 6603-2 | 896 N | ||
| ISO 6603-2 | 776 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | IEC 60250 | 4.00 | |
| IEC 60250 | 3.60 | ||
| Dissipation Factor | IEC 60250 | 8E-03 | |
| IEC 60250 | 0.016 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 245 °C | |
| ISO 75-2/C | 125 °C | ||
| vicat | ISO 306/B50 | >230 °C | |
| ISO 306/B120 | 254 °C | ||
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 3E-05 cm/cm/°C | |
| ISO 11359-2 | 9E-05 cm/cm/°C | ||
| Heat distortion temperature | ISO 75-2/B | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.