PEI

PEI ULTEM™ AUT195 BK1343M SABIC INNOVATIVE US

193

Unit Price:US$ 16,964 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High transparency｜high definition
Application Areas:Electrical appliances｜Automotive Applications
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap	3.20mm	ASTM D256	2100 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,100mmSpan	ASTM D790	145 Mpa
Bending modulus		ISO 178	3100 Mpa
Bending modulus	Bending modulus	100mmSpan	ASTM D790	3170 Mpa
elongation	Break	ASTM D638	70 %
tensile strength	Yield	ASTM D638	96.5 Mpa
Tensile modulus		ISO 527-2/1	3000 Mpa

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ISO 8302	0.23 W/m/K
Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	6E-05 cm/cm/°C
Vicat softening temperature		ISO 306/B120	205 °C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	180 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	190 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	195 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.90 %
Shrinkage rate	TD2	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	340°C/5.0kg	ISO 1133	16.0 cm3/10min
melt mass-flow rate	337°C/6.6kg	ASTM D1238	24 g/10min

Supplementary Information	Test Condition	Test Method	Test Result
Metallic haze	起始	Internal Method	195 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ AUT195 BK1343M SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet