PC LEXAN™ 945A-116 SABIC INNOVATIVE CHONGQING

293

Unit Price:US$ 2,805 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
85.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Bromine free｜currency
Application Areas:Plastic bag｜Lawn equipment｜Garden equipment｜Outdoor applications｜Architectural application field｜medicine｜Electrical field｜Electronic field｜Engine hood parts｜Liquid handling｜Electrical appliances｜Automotive External Parts｜Lighting applications
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	73.4 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.1mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	875 °C
Extreme Oxygen Index		ISO 4589-2	35 %
UL flame retardant rating	0.8mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	101 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2340 Mpa
elongation	Break	ASTM D638	130 %
elongation	elongation	Yield	ASTM D638	6.0 %
tensile strength	Break	ASTM D638	65.5 Mpa
tensile strength	tensile strength	Yield	ASTM D638	62.1 Mpa
Tensile modulus		ASTM D638	2280 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	130 °C
RTI Imp		UL 746	120 °C
RTI Elec		UL 746	130 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Vicat softening temperature		ASTM D15255	143 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	127 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	138 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.60-0.80 %
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 2
High voltage arc tracing rate	HVTR	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 3
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Arc resistance		ASTM D495	PLC7

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.