thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa,未退火	ISO 75-2/B	158 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa,未退火	ISO 75-2/A	148 °C
vicat		ASTM D1525	139 °C
vicat	vicat	雾化 - 16 hr，100℃	DIN 75201	1.0 mg

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230℃/2.16 kg	ISO 1183	4.0 g/10 min
shrinkage rate	2.00 mm	内部方法	0.90 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	7500 Mpa
tensile strength	断裂	ISO 527-2/50	110 Mpa
	tensile strength	拉伸应变，断裂	ISO 527-2/50	3.0 %
		tensile strength	弯曲模量	ISO 178	6500 Mpa
			tensile strength	弯曲应力	ISO 868	145 Mpa
				tensile strength	简支梁缺口冲击强度，-20℃	ISO 179/1eA	10 kJ/m²
				tensile strength	tensile strength	23℃	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	-20℃	ISO 179/1eU	54 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	59 kJ/m²
Impact strength of cantilever beam gap	-20℃	ISO 180/1A	9.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ISO 180/1A	11 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.