PC LEXAN™ EXL1810T-701 SABIC INNOVATIVE SAUDI
215
- Unit Price:US$ 3,289 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:18MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
- Application Areas:Plastic bag｜3D printing application｜Electronic and Electrical Applications
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | L -Sale | ISO 2039-2 | 90 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 120 °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9 | ISO 75-2/Af | 117 °C | |
| Vicat softening temperature | -- | ASTM D152510 | 138 °C |
| -- | ISO 306/B50 | 137 °C | |
| -- | ISO 306/B120 | 140 °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | Flow : -40 to 95°C | ASTM E831 | 6.5E-5 cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 6.5E-5 cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 7.4E-5 cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 7.4E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 825 °C |
| 3.0 mm | IEC 60695-2-13 | 850 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 2540 μm | ASTM D1003 | 82.0 % |
| turbidity | 2540 μm | ASTM D1003 | 3.0 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 35 g/10 min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 33.0 cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | Internal Method | 0.40 - 0.80 % |
| Across FlowFlow : 3.20 mm | Internal Method | 0.40 - 0.80 % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.12 % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.090 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Mold temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2360 Mpa |
| -- | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | Yield3 | ASTM D638 | 59.0 Mpa |
| Yield | ISO 527-2/50 | 59.0 Mpa | |
| Break3 | ASTM D638 | 58.0 Mpa | |
| Break | ISO 527-2/50 | 56.0 Mpa | |
| elongation | Yield3 | ASTM D638 | 5.8 % |
| Yield | ISO 527-2/50 | 5.4 % | |
| Break3 | ASTM D638 | 120 % | |
| Break | ISO 527-2/50 | 120 % | |
| Bending modulus | 50.0 mm Span4 | ASTM D790 | 2350 Mpa |
| --5 | ISO 178 | 2250 Mpa | |
| bending strength | --5,6 | ISO 178 | 92.0 Mpa |
| Yield, 50.0 mm Span4 | ASTM D790 | 99.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 40 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 79.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.