PA66 A20V25 BK SOLVAY SHANGHAI

280
  • Unit Price:US$ 5,655 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Enhanced level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU50 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU55 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.8 mmUL 94V-0
UL flame retardant rating1.6 mmUL 94V-0
UL flame retardant rating3.2 mmUL 94V-0
Burning wire flammability index0.8 mmIEC 60695-2-12960 °C
Burning wire flammability index1.6 mmIEC 60695-2-12960 °C
Burning wire flammability index3.2 mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.6 mmIEC 60695-2-13725 °C
Extreme Oxygen IndexISO 4589-231 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/1A9400 Mpa
tensile strengthBreak, 23°CISO 527-2/1A150 Mpa
Tensile strainBreak, 23°CISO 527-22.5 %
Bending modulus23°CISO 1788500 Mpa
bending strength23°CISO 178255 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature80 °C
Suggested maximum moisture content0.20 %
Temperature at the rear of the barrel265 to 275 °C
Temperature in the middle of the barrel270 to 280 °C
Temperature at the front of the material cylinder280 to 290 °C
Mold temperature60 to 90 °C
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/Af244 °C
Melting temperatureISO 11357-3263 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate横向FlowISO 294-41.2 %
Shrinkage rateFlowISO 294-40.35 %
Water absorption rate24 hr, 23°CISO 620.75 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 622.1 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931.0E+13 ohms
Volume resistivityIEC 600931.0E+15 ohms·cm
Dielectric strength0.800 mmIEC 60243-130 KV/mm
Relative permittivityIEC 602503.40
Dissipation factorIEC 602500.020
Compared to the anti leakage trace indexSolution AIEC 60112PLC 1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.