PA6 Durethan®  BKV215 LANXESS GERMANY

359
  • Unit Price:US$ 4,222 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Cold resistant grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU80 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU70 kJ/m²
Multi axis Instrumented Impact Energy-30°CISO 6603-24.80 J
Multi axis Instrumented Impact Energy23°CISO 6603-213.0 J
Multi axis Instrumented Peak Impact Force-30°CISO 6603-2650 N
Multi axis Instrumented Peak Impact Force23°CISO 6603-21000 N
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.6mmUL 94HB
UL flame retardant rating3.2mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12650 °C
Extreme Oxygen IndexISO 4589-222 %
BurningBehaviorISO 3795passed
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/14500 Mpa
tensile strengthBreak,23°CISO 527-2/585.0 Mpa
Tensile strainBreak,23°CISO 527-2/54.5 %
Bending modulus23°CISO 178/A4000 Mpa
bending strength3.5%Strain,23°CISO 178/A125 Mpa
bending strength23°C4ISO 178/A130 Mpa
Bending strain23°CISO 178/A5.0 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C60.0 °C
Vicat softening temperature--ISO 306/B50200 °C
Vicat softening temperature--ISO 306/B120200 °C
Melting temperatureISO 11357-3214 °C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-24E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-21.5E-04 cm/cm/°C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B205 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A175 °C
Physical propertiesTest ConditionTest MethodTest Result
Apparent densityISO 600.60 g/cm³
Shrinkage rateTD:280°C,2.00mm2ISO 25770.61 %
Shrinkage rateTD:120°C,4hr,2.00mm3ISO 25770.15 %
Shrinkage rateMD:280°C,2.00mm2ISO 25770.59 %
Shrinkage rateMD:120°C,4hr,2.00mm3ISO 25770.14 %
Water absorption rateSaturation,23°CISO 627.0 %
Water absorption rateEquilibrium,23°C,50%RHISO 622.0 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931E+15 ohms
Volume resistivity23°CIEC 600931E+13 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-143 KV/mm
Relative permittivity23°C,100HzIEC 602503.50
Relative permittivity23°C,1MHzIEC 602503.20
Dissipation factor23°C,100HzIEC 602506E-03
Dissipation factor23°C,1MHzIEC 602500.015
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 0
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1110 Mpa
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA6/66HI.GR.14-040.GF15
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.