Material Properties:Filler: Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:--
Color:--
Grade:Injection grade
Technical Data Sheet
hardness
Test Condition
Test Method
Test Result
Ball Pressure Test
ISO 2039-1
230 Mpa
thermal performance
Test Condition
Test Method
Test Result
Vicat softening temperature
ISO 306/B120
>230 °C
Melting temperature
ISO 11357-3
263 °C
Linear coefficient of thermal expansion
MD：23to55°C
ISO 11359-2
2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD：23to55°C
ISO 11359-2
1E-04 cm/cm/°C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
250 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
250 °C
Hot deformation temperature
8.0MPa,Unannealed
ISO 75-2/C
135 °C
flammability
Test Condition
Test Method
Test Result
UL flame retardant rating
1.6mm
UL 94
HB
UL flame retardant rating
3.2mm
UL 94
HB
Burning wire flammability index
2.0mm
IEC 60695-2-12
600 °C
Extreme Oxygen Index
ISO 4589-2
23 %
Supplementary Information
Test Condition
Test Method
Test Result
ISO Shortcut
ISO 1874
PA66.GR.14-110.GF30
Electrical performance
Test Condition
Test Method
Test Result
Surface resistivity
IEC 60093
1E+14 ohms
Volume resistivity
23°C
IEC 60093
1E+15 ohms·cm
Dielectric strength
23°C,1.00mm
IEC 60243-1
40 KV/mm
Relative permittivity
23°C,100Hz
IEC 60250
4.00
Relative permittivity
23°C,1MHz
IEC 60250
4.00
Dissipation factor
23°C,100Hz
IEC 60250
9E-03
Dissipation factor
23°C,1MHz
IEC 60250
0.018
Compared to the anti leakage trace index
SolutionA
IEC 60112
PLC 0
Physical properties
Test Condition
Test Method
Test Result
Apparent density
ISO 60
0.70 g/cm³
Shrinkage rate
TD:280°C,3.00mm2
ISO 2577
1.5 %
Shrinkage rate
TD:120°C,2hr,3.00mm3
ISO 294-4
0.050 %
Shrinkage rate
MD:280°C,3.00mm2
ISO 2577
0.35 %
Shrinkage rate
MD:120°C,2hr,3.00mm3
ISO 2577
0.040 %
Water absorption rate
Saturation,23°C
ISO 62
5.5 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
2.0 %
mechanical properties
Test Condition
Test Method
Test Result
tensile strength
Break,23°C
ASTM D638
179 Mpa
tensile strength
Break,23°C
ISO 527-2/5
185 Mpa
elongation
Break,23°C
ASTM D638
3.0 %
Tensile strain
Break,23°C
ISO 527-2/5
3.0 %
Bending modulus
23°C
ASTM D790
841 Mpa
Bending modulus
23°C
ISO 178/A
8400 Mpa
bending strength
23°C
ASTM D790
290 Mpa
bending strength
3.5%Strain
ISO 178/A
-- Mpa
bending strength
23°C
ISO 178
290 Mpa
bending strength
FlexuralStrainatFlexuralStrength5(23°C)
4.0 %
Tensile modulus
23°C
ASTM D638
10300 Mpa
Tensile modulus
23°C
ISO 527-2/1
10600 Mpa
impact performance
Test Condition
Test Method
Test Result
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
70 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
90 kJ/m²
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.