PC/ABS LNP™ FARADEX™ NX07344-NC SABIC INNOVATIVE NANSHA
203
- Unit Price:US$ 8,478 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility|High impact resistance
- Application Areas:Automotive interior parts|Electrical applications
- Color:--
- Grade:Enhanced fiber grade
Technical Data Sheet
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Flow: 23 to 60 ° C | 23到60℃ | ISO 11359-2 | 2.9E-05 cm/cm/°C |
Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 5.8E-05 cm/cm/°C |
Horizontal: 23 to 60 ° C | 横向, 23到60℃ | ISO 11359-2 | 7.4E-05 cm/cm/°C |
1.8MPa, Unanealed, 3.20mm | ASTM D648 | 94.0 °C | |
1.8MPa, Unanealed, 6.40mm | ASTM D648 | 96.0 °C | |
1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 96.0 °C | |
Flow: -40 to 40 ° C | ASTME831 | 3.1E-05 cm/cm/°C |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | 1.50mm | UL 94 | V-0 |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.6 kJ/m² |
-30°C | ASTM D256 | 44 J/m | |
23°C | ASTM D256 | 60 J/m | |
-30°C | ISO 180/1A | 5.3 kJ/m² | |
23°C | ISO 180/1A | 6.0 kJ/m² | |
-30°C | ASTM D4812 | 330 J/m | |
23°C | ASTM D4812 | 350 J/m | |
-30°C | ISO 180/1U | 21 kJ/m² | |
23°C | ISO 180/1U | 21 kJ/m² | |
23°C,TotalEnergy | ASTM D3763 | 11.5 J |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface Resistivity | ASTM D257 | 1.0E+3-1.0E+6 ohms | |
volume resistivity | ASTM D257 | 1.0E+4-1.0E+6 ohms·cm | |
StaticDecay | FTMS101B | 10 msec | |
Electromagnetic shielding effectiveness (EMI) | 1.50mm | 内部方法 | 47to53 dB |
3.00mm | 内部方法 | 60to70 dB |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
shrinkage rate | MD | 内部方法 | 0.38 % |
TD | 内部方法 | 0.46 % | |
24hr,50%RH | ASTM D570 | 0.080 % | |
Balance, 23 ° C, 50% RH | ISO 62 | 0.040 % |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Fracture, 50.0mm span | ASTM D790 | 90.0 Mpa | |
Fracture bending strain | ISO 178 | 2.8 % | |
--1 | ASTM D638 | 6000 Mpa | |
fracture | ASTM D638 | 60.0 Mpa | |
ISO 527-2/5 | 62.0 Mpa | ||
ASTM D638 | 1.8 % | ||
ISO 527-2/5 | 1.8 % | ||
flexural modulus | 50.0mm跨距 | ASTM D790 | 5300 Mpa |
--5 | ISO 178 | 105 Mpa | |
Yield, 50.0mm span | ASTM D790 | 90.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.