ABS POLYLAC® PA-705 TAIWAN CHIMEI

544

Unit Price:US$ 1,792 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Kaoshiung port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS POLYLAC® PA-705 ZHENJIANG CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜High mobility｜High temperature resistance
Application Areas:Lighting fixtures｜Office supplies｜Casters｜Household goods
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Huangdu Index		ASTM D-1925	8.5(±)1.25
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃*10kg	ASTM D-1238	27	g/10min
melt mass-flow rate	melt mass-flow rate	200℃*5kg	ASTM D-1238	2.7	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D-785	110	R scale
bending strength	2.8mm/min	ASTM D-790	680	kg/cm
Bending modulus	2.8mm/min	ASTM D-790	24000	kg/cm
Elongation at Break	6mm/min	ASTM D-638	20	%
tensile strength	6mm/min	ASTM D-638	450	kg/cm
Impact strength of cantilever beam gap	1/4"	ASTM D-256	16	kg-cm/cm
Bending modulus		ASTM D790/ISO 178	24000	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	110
elongation		ASTM D638/ISO 527	20	%
tensile strength		ASTM D638/ISO 527	450	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	16	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	680	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	1kg*50℃/hr	ASTM D-792	104	°C
Vicat softening temperature	Vicat softening temperature		ASTM D1525/ISO R306	104	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	27	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	2.7	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.