MVLDPE

MVLDPE DOWLEX™ 4404G STYRON US

373

Unit Price:US$ 2,420 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:optical performance ｜High toughness and optical performance｜Certified by Canadian HPFB
Application Areas:film｜Mainly used for packaging
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity		ASTM D-1003	1.8 %
gloss	45°	ASTM D-2457	90
transparency		ASTM D-1746	99
gloss	45°,20.3μm	ASTM D2457	92
gloss	gloss	45°,50.8μm	ASTM D2457	90
transparency	20.3μm	ASTM D1746	99.0
transparency	transparency	50.8μm	ASTM D1746	99.0
turbidity	20.3μm	ASTM D1003	0.60 %
turbidity	turbidity	50.8μm	ASTM D1003	1.8 %

Basic Performance	Test Condition	Test Method	Test Result
density		ASTM D792	0.904 g/cm³
melt mass-flow rate		ASTM D1238	4 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	MD，3% Secant	ASTM D-882	63 Mpa
Tensile modulus	Tensile modulus	TD，2% Secant	ASTM D-882	63 Mpa
Elongation at Break	MD	ASTM D-882	664 %
Elongation at Break	Elongation at Break	TD	ASTM D-882	714 %
tensile strength	MD，Break	ASTM D-882	33 Mpa
	tensile strength	TD，Break	ASTM D-882	32 Mpa
		tensile strength	Yield,MD	ASTM D-882	7 Mpa
		tensile strength	tensile strength	Yield,TD	ASTM D-882	5 Mpa
Puncture intensity		陶氏企业测试	17 J/cm³

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525	71.1 °C
Vicat softening temperature	Vicat softening temperature		ASTM D-1525	71 °C
Melting temperature		Internal Method	124 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ASTM D1238	4.0 g/10min

film	Test Condition	Test Method	Test Result
Carbon dioxide transmittance	23°C,50.8μm	Internal Method	2000 cm³·mm/m²/atm/24hr
Water vapor permeability	51μm	ASTMF1249	0.85 g·mm/m²/atm/24hr
Oxygen permeability	23°C,51μm	ASTM D3985	450 cm³·mm/m²/atm/24hr
Elmendorf tear strength	TD:51μm	ASTM D1922	1100 g
	Elmendorf tear strength	TD:20μm	ASTM D1922	500 g
		Elmendorf tear strength	MD:51μm	ASTM D1922	960 g
		Elmendorf tear strength	Elmendorf tear strength	MD:20μm	ASTM D1922	330 g
Dart impact	51μm	ASTM D1709B	>850 g
Dart impact	Dart impact	20μm	ASTM D1709B	>850 g
elongation	TD:Break,51μm	ASTM D882	710 %
Thin film puncture strength	20μm	Internal Method	18.9 J/cm³
Thin film puncture strength	Thin film puncture strength	51μm	Internal Method	17.5 J/cm³
Secant modulus	2%Secant,MD:20μm	ASTM D882	58.8 Mpa
	Secant modulus	2%Secant,MD:51μm	ASTM D882	62.6 Mpa
		Secant modulus	2%Secant,TD:20μm	ASTM D882	64.7 Mpa
		Secant modulus	Secant modulus	2%Secant,TD:51μm	ASTM D882	63.0 Mpa
tensile strength	MD:Yield,20μm	ASTM D882	7.00 Mpa
	tensile strength	MD:Yield,51μm	ASTM D882	6.76 Mpa
		tensile strength	TD:Yield,20μm	ASTM D882	4.92 Mpa
			tensile strength	TD:Yield,51μm	ASTM D882	6.34 Mpa
				tensile strength	MD:Break,20μm	ASTM D882	36.9 Mpa
					tensile strength	MD:Break,51μm	ASTM D882	32.6 Mpa
						tensile strength	TD:Break,20μm	ASTM D882	29.1 Mpa
						tensile strength	tensile strength	TD:Break,51μm	ASTM D882	32.4 Mpa
elongation	MD:Break,20μm	ASTM D882	500 %
	elongation	MD:Break,51μm	ASTM D882	660 %
	elongation	elongation	TD:Break,20μm	ASTM D882	710 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

MVLDPE DOWLEX™ 4404G STYRON US

Material Description

Technical Data Sheet Compare

Technical Data Sheet