Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
			高钢性耐热
purpose			自动车部件

Basic performance	Test Condition	Test Method	Test Result
Shrinkage rate			0.3-0.7 %
Water absorption rate			1.4 %

Mechanical properties	Test Method	Test Result
(fracture) elongation rate	ASTM D-638	3（4） %
Flexural modulus	ASTM D-790	120.000（85.000） Kgf/cm
Impact strength of cantilever beam gap	ASTM D-256	13（21） Kgf.cm/cm
tensile strength	ASTM D-638	2000（1600） Kgf/cm
Rockwell hardness	ASTM D-785	96/118（80） M/R
Taber wear rate	ASTM D-1044	1900 mg/1000次
bending strength	ASTM D-790	3200（2400） Kgf/cm
Charpy Notched Impact Strength	ASTM D256/ISO 179	127 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness	ASTM D785	M96
Flexural modulus	ASTM D790/ISO 178	11770 kg·cm/cm(J/M)ft·lb/in
bending strength	ASTM D790/ISO 178	214 kg·cm/cm(J/M)ft·lb/in

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.50
Water absorption rate		ASTM D570/ISO 62	1.4 %

Thermal performance	Test Method	Test Result
UL flame retardant rating	UL 94	HB
Hot deformation temperature (HDT)	ASTM D648	250（260） °C 18.2kgf/cm
Linear expansion coefficient	ASTM D696	3 1e-5/cm.°C
Combustibility (rate)	UL 94	HB
Hot deformation temperature (HDT)	ASTM D648/ISO 75	250 ℃（℉）
Linear expansion coefficient	ASTM D696/ISO 11359	3 mm/mm.℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.