PEI ULTEM™ 4000-7401 SABIC INNOVATIVE US

296

Unit Price:US$ 13,561 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜enhance
Application Areas:Fitness equipment｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.20mm	ASTM D256	170 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	82.7 Mpa
Tensile strain	Break	ASTM D638	1.2 %
Bending modulus	100mmSpan	ASTM D790	8830 Mpa
bending strength	Yield,100mmSpan	ASTM D790	114 Mpa
bending strength	bending strength	Break,100mmSpan	ASTM D790	138 Mpa
Friction coefficient	Steel - Dynamic	ASTM D1894	0.24
Friction coefficient	Friction coefficient	Steel - Static6	ASTM D1894	0.25
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	33.0 mg

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	212 °C
Vicat softening temperature		ASTM D15257	234 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	1.6E-05 cm/cm/°C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	105 °C
RTI Str		UL 746	105 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6kg	ASTM D1238	3.1 g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.30 %
Water absorption rate	24hr	ASTM D570	0.11 %
K (wear) coefficient	--2	Internal Method	62.0
K (wear) coefficient	K (wear) coefficient	--3	Internal Method	1900
limiting pv value		Internal Method	2.1 MPa·m/s

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 4

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	85

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 4000-7401 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet