POM TENAC™ 4013A ASAHI JAPAN

Unit Price:US$ 3,640 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Yiwei Plastic Trading Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Weather resistance｜UV resistance｜Medium viscosity
Application Areas:Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			含UV紫外线吸收剂和其他耐气候助剂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	67	Mpa
Elongation at Break		ASTM D638	55	%
Elongation at Break	Elongation at Break		ASTM D638/ISO 527	55	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	78	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	55	%
bending strength		ASTM D790/ISO 178	98	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	3040	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	94
tensile strength		ASTM D638/ISO 527	67	kg/cm²(MPa)[Lb/in²]
Wear resistance		ASTM D1044	13
Rockwell hardness	-	ASTM D785	120	R
Rockwell hardness	Rockwell hardness	-	ASTM D785	94	M
Impact strength of cantilever beam gap		ASTM D256	78	J/m
Bending modulus		ASTM D790	3040	Mpa
bending strength		ASTM D790	98	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	172	℃（℉）
	Hot deformation temperature	HDT	ASTM D648/ISO 75	136	℃（℉）
		Hot deformation temperature	0.45MPa	ASTM D648	172	°C
		Hot deformation temperature	Hot deformation temperature	1.82MPa	ASTM D648	136	°C
Linear coefficient of thermal expansion		TMA法	10
melt mass-flow rate		ASTM D1238	10	g/10min
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570	0.2	%
Shrinkage rate	Flow	旭化成法	1.8-2.2	%
Shrinkage rate	Shrinkage rate	Across Flow	旭化成法	1.8-2.2	%
melt mass-flow rate		ASTM D1238/ISO 1133	10	g/10min
Shrinkage rate		ASTM D955	1.8-2.2	%
Water absorption rate		ASTM D570/ISO 62	0.2	%
density		ASTM D792/ISO 1183	1.42

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3240 /MT

Supplier Join

Get App

Top

POM TENAC™ 4013A ASAHI JAPAN

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index