ABS TAIRILAC® AG15E3 FORMOSA NINGBO

149

Unit Price:US$ 1,239 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
300MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS TAIRILAC® AG15E3 FCFC TAIWAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜High rigidity
Application Areas:Electrical appliances｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	150	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ISO 180	150	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	78.0	Mpa
bending strength	bending strength	23°C	ASTM D790	78.0	Mpa
Bending modulus	23°C	ISO 178	2750	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	2750	Mpa
tensile strength	Yield,23°C	ISO 527-2	48.0	Mpa
tensile strength	tensile strength	23°C	ASTM D638	48.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/A	103	°C
Vicat softening temperature	Vicat softening temperature		ASTM D15253	103	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	96.0	°C
	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	96.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ISO 75-2/A	86.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	86.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.1	g/10min
density	23°C	ISO 1183	1.05	g/cm³
density	density		ASTM D792	1.05	g/cm³
Shrinkage rate	MD	Internal Method	0.40-0.70	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	21	g/10min
	melt mass-flow rate	200°C/5.0kg	ISO 1133	2.1	g/10min
	melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	21	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	111
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ASTM D785	111

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS TAIRILAC® AG15E3 FORMOSA NINGBO

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index