Material Description
- Material Properties:High sliding｜wear resistant
- Application Areas:Electrical field｜Electronic field｜Engine parts
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| MediumDensity | 0.970 g/cm³ | ||
| Ejection Temperature | 190 °C | ||
| SpecificHeatCapacity of Melt | 2790 J/kg/°C | ||
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 1.4 % | |
| ISO 294-4 | 0.10 % | ||
| ISO 294-4 | 1.4 % | ||
| ISO 294-4 | 0.20 % | ||
| Water absorption rate | ISO 62 | 8.5 % | |
| ISO 62 | 2.6 % | ||
| viscosity number | ISO 307 | 140 cm³/g |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fogging-G-value | ISO 6452 | 1E-04 g | |
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | UL 94 | V-2 | |
| IEC 60695-11-10,-20 | V-2 | ||
| IEC 60695-11-10,-20 | V-2 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 6.50 µgC/g | |
| Odor | VDA270 | 3.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 400 kJ/m² | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 5.5 kJ/m² | |
| ISO 180/1A | 5.5 kJ/m² | ||
| ISO 180/1A | 6.0 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 4.5 kJ/m² | |
| ISO 179/1eA | 6.0 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 300 kJ/m² | |
| ISO 180/1U | 300 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3100 Mpa | |
| Tensile creep modulus | ISO 899-1 | -- Mpa | |
| tensile strength | ISO 527-2 | 82.0 Mpa | |
| Tensile creep modulus | ISO 899-1 | -- Mpa | |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| Tensile strain | ISO 527-2 | 4.5 % | |
| Nominal tensile fracture strain | ISO 527-2 | 20 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO 527-3 | 4.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| IEC 60250 | 3.80 | ||
| IEC 60250 | 3.60 | ||
| Dissipation Factor | IEC 60250 | 0.014 | |
| IEC 60250 | 0.018 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 11359-2 | 1.1E-04 cm/cm/°C | ||
| Effective thermal diffusivity coefficient | 5E-08 m²/s | ||
| ISO 11359-2 | 1E-04 cm/cm/°C | ||
| vicat | ISO 306/B50 | 240 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/A | 70.0 °C | |
| ISO 75-2/B | 190 °C | ||
| melting temperature | ISO 11357-3 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.