PA66 Zytel®  101F NC010 DUPONT SINGAPORE

510
  • Unit Price:US$ 2,841 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    346.5MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High sliding｜wear resistant
  • Application Areas:Electrical field｜Electronic field｜Engine parts
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A5.5 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A5.5 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eU400 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA4.5 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U300 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U300 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94V-2
FMVSS flammabilityFMVSS302SE
Extreme Oxygen IndexISO 4589-228 %
Fogging-G-valuecondensateISO 64521E-04 g
UL flame retardant rating0.71mmIEC 60695-11-10,-20V-2
UL flame retardant rating1.5mmIEC 60695-11-10,-20V-2
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-23100 Mpa
Tensile creep modulus1hrISO 899-1-- Mpa
tensile strengthYieldISO 527-282.0 Mpa
Tensile creep modulus1000hrISO 899-1-- Mpa
Bending modulusISO 1782800 Mpa
Tensile strainYieldISO 527-24.5 %
Nominal tensile fracture strainISO 527-220 %
thermal performanceTest ConditionTest MethodTest Result
Effective thermal diffusivity coefficient5E-08 m²/s
Linear coefficient of thermal expansionTDISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionMDISO 11359-21E-04 cm/cm/°C
Vicat softening temperatureISO 306/B50240 °C
Glass transition temperatureISO 11357-260.0 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A70.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B190 °C
Melting temperatureISO 11357-3262 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTD:80°C,48hrISO 294-40.10 %
Shrinkage rateMDISO 294-41.4 %
Shrinkage rateTDISO 294-41.4 %
densityISO 11831.14 g/cm³
SpecificHeatCapacity of Melt2790 J/kg/°C
Top out temperature190 °C
MediumDensity0.970 g/cm³
ThermalConductivityofMelt0.16 W/m/K
Shrinkage rateMD:80°C,48hrISO 294-40.20 %
Water absorption rateSaturation,23°C,2.00mmISO 628.5 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 622.6 %
StickinessISO 307140 cm³/g
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor1MHzIEC 602500.018
Dissipation factor100HzIEC 602500.014
Relative permittivity1MHzIEC 602503.60
Relative permittivity100HzIEC 602503.80
Dielectric strengthIEC 60243-132 KV/mm
Volume resistivityIEC 600931E+15 ohms·cm
filmTest ConditionTest MethodTest Result
Tensile strainYield，MDISO 527-34.5 %
Supplementary InformationTest ConditionTest MethodTest Result
OdorVDA2703.00
EmissionofOrganicCompoundsVDA2776.50 µgC/g
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.