ABS POLYLAC® PA-749SK ZHENJIANG CHIMEI

722

Unit Price:US$ 2,070 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
166.6MT
Delivery Terms:
FOB
Port of Loading :
Lianyungang port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS TAIRILAC® AG12A0 FCFC TAIWAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength
Application Areas:Plate
Color:--
Grade:Impact resistant grade

Material Certification

SGS

MSDS

RoHS

TDS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
purpose			冰箱板材
characteristic			高冲击性押出级
machinability	Test Condition	Test Method	Test Result	Test Unit
Dry conditions			80℃.2-3小时
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃ 10kg	ISO 1133	5	g/10min
melt mass-flow rate	melt mass-flow rate	200℃ 5kg	ASTM D-1238	0.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D-790	620	kg/cm2
Elongation at Break		ASTM D-790	40	%
Bending modulus		ASTM D-790	2.1	104kg/cm2
Rockwell hardness		ASTM D-785	102	R
tensile strength		ASTM D-638	390	kg/cm2
Impact strength of cantilever beam gap	1/8"	ASTM D-256	40	kg.cm/cm
	Impact strength of cantilever beam gap	1/4"	ASTM D-256	35	kg.cm/cm
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	37.5(6.9)	kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	33(6.1)	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	620(8800)	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2.2(3.1)	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-108
elongation		ASTM D638/ISO 527	30	%
tensile strength		ASTM D638/ISO 527	420(5950)	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility		File NO.E196075	1/16"HB
Vicat softening temperature		ASTM D-1525	103(217)	℃(°F)
Hot deformation temperature	Unannealed	ASTM D-648	87(189)	℃(°F)
Hot deformation temperature	Hot deformation temperature	Annealed	ASTM D-648	97(207)	℃(°F)
Vicat softening temperature		ASTM D1525/ISO R306	103(217)	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	86(187)	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	97(207)	℃（℉）
Combustibility (rate)		UL 94	1.6mm
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	9	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	0.8	g/10min
density		ASTM D792/ISO 1183	1.03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Weisu	US$ 2030 /MT
Guangdong Mingxin	US$ 2030 /MT
Shantou Qiheng Trading	US$ 2040 /MT
Dongguan Runfeng Plastic	US$ 2050 /MT
Guangdong Sinan	US$ 2050 /MT

Supplier Join

Get App

Top

ABS POLYLAC® PA-749SK ZHENJIANG CHIMEI

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index