Material Properties:High rigidity｜High mobility｜Chemical resistance｜Filler: Carbon fiber reinforced material｜30% filler by weight
Application Areas:Vehicle accessories｜Engine parts｜Industrial applications｜Cam｜Metal substitution｜Power/Other Tools｜Application in the automotive field｜Bushing｜Lawn and garden equipment｜Phone｜Electrical/Electronic Applications｜Parts under the hood of a car｜Machine/mechanical components｜Camera applications｜Electrical appliances｜Vehicle electronics｜Home appliance components｜furniture
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		内部方法	0.030-0.10 %
Water absorption rate		ISO 62	0.22 %
Water absorption rate	Water absorption rate		内部方法	2.0 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
Limiting Oxygen Index		ISO 4589-2	23 %

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	26000 Mpa
tensile strength	ISO 527-2	250 Mpa
Tensile strain	ISO 527-2	1.3 %
Flexural modulus	ISO 178	23000 Mpa
bending strength	ISO 178	360 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	36 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	3E+03 ohms·cm
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	230 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.