PC 241R-WH6D069 SABIC INNOVATIVE NANSHA
144
- Unit Price:US$ 2,892 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:38MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTM D785 | 118 |
| M计秤 | ASTM D785 | 70 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.27 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 132 °C |
| vicat | ASTM D15255 | 154 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 138 °C |
| RTI Str | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 6.0mm | UL 94 | V-0 |
| 1.1mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 578 kJ/m² | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 63.8 J |
| 23°C | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 3200 J/m |
| 23°C | ASTM D256 | 800 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| 60Hz | ASTM D150 | 9E-04 | |
| 50Hz | ASTM D150 | 9E-04 | |
| dielectric constant | 1MHz | ASTM D150 | 2.96 |
| 60Hz | ASTM D150 | 3.17 | |
| 50Hz | ASTM D150 | 3.17 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
| 24hr | ASTM D570 | 0.15 % | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| density | ASTM D792 | 1.19 g/cm³ | |
| ASTM D792 | 1.20 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.5 Mpa |
| elongation | 断裂 | ASTM D638 | 130 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| tensile strength | 断裂 | ASTM D638 | 68.9 Mpa |
| 屈服 | ASTM D638 | 62.1 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App
Top