Material Description

Material Properties:Glass fiber reinforced｜Non chloro non bromine flame retardant
Application Areas:Electronic and Electrical Applications｜Plastic bag
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	22.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	710 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.600mm	UL 94	V-0
	UL flame retardant rating	0.400mm	UL 94	V-1
	UL flame retardant rating	UL flame retardant rating	0.300mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Fracture, 50.0mm span		ASTM D790	131 Mpa
--6		ISO 178	133 Mpa
--1		ASTM D638	4400 Mpa
crack		ASTM D638	83.0 Mpa
	crack		ISO 527-2/5	82.0 Mpa
		crack		ASTM D638	3.6 %
		crack	crack		ISO 527-2/5	3.6 %
50.0mm span		ASTM D790	4070 Mpa
--5		ISO 178	4010 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	3.4E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	121 °C
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7.7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	27.0 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	13.0 cm3/10min
melt mass-flow rate	300°C/2.16kg	ASTM D1238	29 g/10min
melt mass-flow rate	melt mass-flow rate	300°C/1.2kg	ASTM D1238	14 g/10min
Shrinkage rate	MD:24hr	ASTM D955	0.30-0.50 %
Shrinkage rate	Shrinkage rate	TD:24hr	ASTM D955	0.30-0.50 %
Water absorption rate	Saturation,23°C	ISO 62	0.080 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	10.0GHz	Internal Method	6.9E-03
	Dissipation factor	5.00GHz	Internal Method	6.9E-03
		Dissipation factor	1.90GHz	Internal Method	6.5E-03
		Dissipation factor	Dissipation factor	1.10GHz	Internal Method	6.7E-03
Dielectric constant	10.0GHz	Internal Method	3.05
	Dielectric constant	5.00GHz	Internal Method	3.06
		Dielectric constant	1.90GHz	Internal Method	3.06
		Dielectric constant	Dielectric constant	1.10GHz	Internal Method	3.07

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.