PA66 Zytel®  73G30HSL BK416 DUPONT JAPAN

289
  • Unit Price:US$ 2,302 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Thermal stability｜Filler: Glass fiber reinforced material｜30% filler by weight
  • Application Areas:Automotive Applications｜Home appliance components
  • Color:--
  • Grade:Wear resistant grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA10 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA16 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU80 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A15 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U80 kJ/m²
Multi axis Instrumented Impact Energy23°CISO 6603-23.50 J
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379550 mm/min
UL flame retardant rating0.75mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating0.75mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
Extreme Oxygen IndexISO 4589-221 %
FMVSS flammabilityFMVSS302B
AtomizationF-value(refraction)ISO 645295 %
AtomizationG-value(condensate)ISO 64521E-04 g
mechanical propertiesTest ConditionTest MethodTest Result
Tensile creep modulus1000hrISO 899-1-- Mpa
Bending modulusISO 1788500 Mpa
bending strengthISO 178280 Mpa
Tensile modulusISO 527-29500 Mpa
tensile strengthBreakISO 527-2190 Mpa
Tensile strainBreakISO 527-23.5 %
Tensile creep modulus1hrISO 899-1-- Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B220 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A210 °C
Glass transition temperatureISO 11357-260.0 °C
Vicat softening temperatureISO 306/B50215 °C
Melting temperatureISO 11357-3221 °C
Linear coefficient of thermal expansionMDISO 11359-22.6E-05 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-27.5E-05 cm/cm/°C
Effective thermal diffusivity coefficient9.1E-08 m²/s
Physical propertiesTest ConditionTest MethodTest Result
MediumDensity1.20 g/cm³
SpecificHeatCapacity of Melt2280 J/kg/°C
ThermalConductivityofMelt0.26 W/m/K
densityISO 11831.36 g/cm³
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113315.0 cm3/10min
Shrinkage rateTDISO 294-40.60 %
Shrinkage rateMDISO 294-40.20 %
Water absorption rateSaturation,23°C,2.00mmISO 626.3 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 621.9 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleISO 2039-2121
Ball Pressure TestH961/30ISO 2039-1230 Mpa
Supplementary InformationTest ConditionTest MethodTest Result
EmissionofOrganicCompoundsVDA2778.50 µgC/g
OdorVDA2703.50
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.