PPO/PA NORYL GTX™ GTX830-111 SABIC INNOVATIVE US
314
- Unit Price:US$ 4,149 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:65MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:dimensional stability ｜High temperature resistance｜Hydrolysis resistance
- Application Areas:Electrical applications｜Industrial machinery
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 254 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 240 °C | |
| vicat | ASTM D15255 | 248 °C | |
| Linear coefficient of thermal expansion | -20 到 150°C，流动 | ASTM E831 | 2.0E-5 - 3.1E-5 cm/cm/°C |
| RTI Elec | UL 746 | 50.0 °C | |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.20 - 0.30 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.65 - 0.85 % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.50 % |
| 平衡, 50% RH | ASTM D570 | 1.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 2 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 1 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 95 to 105 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.070 % | ||
| Suggested injection volume | 30 to 50 % | ||
| Temperature at the rear of the barrel | 265 to 305 °C | ||
| Temperature in the middle of the barrel | 270 to 305 °C | ||
| Temperature at the front of the material cylinder | 275 to 305 °C | ||
| Spray nozzle temperature | 280 to 305 °C | ||
| Processing (melt) temperature | 280 to 305 °C | ||
| mold temperature | 75 to 120 °C | ||
| Back pressure | 0.300 to 1.40 Mpa | ||
| screw speed | 20 to 100 rpm | ||
| Exhaust hole depth | 0.013 to 0.038 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 151 Mpa |
| 断裂 | ASTM D638 | 158 Mpa | |
| elongation | 断裂 | ASTM D638 | 7.0 % |
| flexural modulus | 100 mm 跨距 | ASTM D790 | 8580 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 248 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.