ASA/PC GELOY™ XP4034 SABIC INNOVATIVE US
353
- Unit Price:US$ 2,835 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:60MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:ASA/PC GELOY™ XP4034 SABIC INNOVATIVE NANSHA
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Thermal stability｜Antistatic｜Weather resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 5.0 g/10 min | |
| ASTM D1238 | 14 g/10 min | ||
| ASTM D1238 | 24 g/10 min | ||
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % | |
| 内部方法 | 0.50 - 0.70 % | ||
| Water absorption rate | ASTM D570 | 0.25 % | |
| Outdoor applicability | UL 746C | f2 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 110 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D523 | 94 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| tensile strength | ASTM D638 | 62.0 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ISO 527-2/50 | 50.0 Mpa | ||
| Tensile strain | ISO 527-2/50 | 4.5 % | |
| ASTM D638 | 25 % | ||
| ISO 527-2/50 | 130 % | ||
| Flexural modulus | ASTM D790 | 2510 Mpa | |
| ISO 178 | 2500 Mpa | ||
| bending strength | ISO 178 | 75.0 Mpa | |
| ASTM D790 | 88.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 30.0 J | |
| ASTM D3763 | 47.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 95 to 105 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Spray nozzle temperature | 245 to 265 °C | ||
| Processing (melt) temperature | 260 to 275 °C | ||
| Temperature | 55 to 70 °C | ||
| Back pressure | 0.300 to 1.00 Mpa | ||
| screw speed | 30 to 80 rpm | ||
| Exhaust hole depth | 0.038 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 115 °C | |
| ISO 75-2/Bf | 116 °C | ||
| ASTM D648 | 104 °C | ||
| ISO 75-2/Af | 98.0 °C | ||
| vicat | ISO 306/B50 | 113 °C | |
| ASTM E831 | 7.2E-5 cm/cm/°C | ||
| ASTM E831 | 7.2E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.