POM

POM Delrin®  900P DUPONT SHENZHEN

355
  • Unit Price:US$ 5,451 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    135MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:wear resistant｜High rigidity｜high strength｜enhance｜High impact resistance｜High mobility
  • Application Areas:Fiber grade｜Thin walled products
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU200 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU200 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA8.0 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA7.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A7.0 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A8.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379520 mm/min
UL flame retardant rating0.8mmUL 94HB
Extreme Oxygen IndexISO 4589-223 %
FMVSS flammabilityFMVSS302B
AtomizationF-value(refraction)ISO 645295 %
AtomizationG-value(condensate)ISO 64522E-04 g
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating0.8mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
mechanical propertiesTest ConditionTest MethodTest Result
Friction coefficientvs.Itself-Dynamic,1hrASTM D18940.25
Bending modulusISO 1783000 Mpa
Tensile creep modulus1000hrISO 899-11500 Mpa
Tensile creep modulus1hrISO 899-12800 Mpa
Nominal tensile fracture strainISO 527-223 %
Tensile modulusISO 527-23300 Mpa
tensile strengthYieldISO 527-271.0 Mpa
Tensile strainYieldISO 527-212 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMD：23to55°CASTME8311E-04 cm/cm/°C
Melting temperatureISO 11357-3178 °C
Vicat softening temperatureISO 306/B50160 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A94.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B162 °C
Effective thermal diffusivity coefficient8E-08 m²/s
AnnealingTime-Optional30.0 min/mm
AnnealingTemperature160 °C
Linear coefficient of thermal expansionTDISO 11359-21.2E-04 cm/cm/°C
Linear coefficient of thermal expansionMDISO 11359-21.2E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
densityISO 11831.42 g/cm³
melt mass-flow rateISO 113325 g/10min
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 113321.0 cm3/10min
Shrinkage rateTDISO 294-41.9 %
Shrinkage rateMDISO 294-41.9 %
Water absorption rateSaturation,23°C,2.00mmISO 621.4 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.40 %
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityIEC 600931E+14 ohms·cm
Relative permittivity100HzIEC 602503.80
Relative permittivity1MHzIEC 602503.80
Surface resistivityIEC 60093>1.0E+15 ohms
Compared to the anti leakage trace indexIEC 60112 V
Hot wire ignition0.750mmUL 746 sec
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-SaleISO 2039-2120
Rockwell hardnessM-SaleISO 2039-292
Supplementary InformationTest ConditionTest MethodTest Result
EmissionofOrganicCompoundsVDA2774.30 µgC/g
EmissionVDA275<8.00 mg/kg
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.