PC/ABS

PC/ABS WONDERLOY® PC-385 TAIWAN CHIMEI

402

Unit Price:US$ 2,868 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
88MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PC/ABS WONDERLOY® PC-385 ZHENJIANG CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜High impact resistance
Application Areas:Automotive Applications｜Electrical applications｜currency
Color:--
Grade:Injection grade

Material Certification

MSDS

RoHS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180	45 kJ/m²
	Impact strength of cantilever beam gap	-30°C,3.18mm	ASTM D256	490 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	590 J/m
Charpy Notched Impact Strength	23°C	ISO 179	55 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	55 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	45 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	2300 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	2300 Mpa
Tensile strain	Break	ISO 527-2/50	130 %
Tensile strain	Tensile strain	Break,23°C	ASTM D638	90 %
bending strength		ISO 178	85.0 Mpa
bending strength	bending strength	23°C	ASTM D790	78.5 Mpa
tensile strength	Yield,23°C	ASTM D638	53.0 Mpa
	tensile strength	Yield	ISO 527-2/50	55.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	57.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	7.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	125 °C
	Vicat softening temperature	--	ISO 306/A50	140 °C
		Vicat softening temperature	--	ASTM D152511	133 °C
		Vicat softening temperature	Vicat softening temperature	--	ASTM D152510	140 °C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	108 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	118 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	110 °C

Physical properties	Test Condition	Test Method	Test Result
density	比重	ASTM D792	1.15 g/cm³
density	density	23°C	ISO 1183	1.15 g/cm³
melt mass-flow rate	260°C/5.0kg	ASTM D1238	20 g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ISO 1133	20 g/10min
Spiral flow length		Internal Method	28.0 CM
Shrinkage rate	MD	ASTM D955	0.40-0.60 %
Shrinkage rate	Shrinkage rate		ISO 2577	0.40-0.60 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1MHz	IEC 60250	3.00
Volume resistivity		IEC 60093	1E+18 ohms·cm
Surface resistivity		IEC 60093	1E+16 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ISO 2039-2	114
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS WONDERLOY® PC-385 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet