PBT Cristin® SK602 GY042D DUPONT USA
170
- Unit Price:US$ 3,763 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜15% filler by weight｜15% filler by weight
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 6.00 mm | UL 94 | HB |
| 3.00 mm | UL 94 | HB | |
| 1.50 mm | UL 94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 200 °C |
| melting temperature | ISO 11357-3 | 225 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 30 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 3.0mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| Fogging-G-value | condensate | ISO 6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 140 µgC/g | |
| Odor | VDA270 | 3.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.0 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm³ | |
| ISO 1183 | 1.41 g/cm³ | ||
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.40 % | |
| MDLength2(2.00mm) | ISO 294-4 | 360 mm | |
| Ejection Temperature | 170 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 100Hz | IEC 60250 | 7E-04 |
| 1MHz | IEC 60250 | 0.017 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.70 |
| 1MHz | IEC 60250 | 3.60 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 0.00 mm, 23 ℃, Injection Molded | ISO 527-1 | 5700 MPa |
| ISO 527-2 | 5800 Mpa | ||
| tensile strength | 断裂 | ISO 527-2 | 109 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.