impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,3.20mm,总能量	ASTM D3763	58.8	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	V-0
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	960	°C
Extreme Oxygen Index		ASTMD2863	35	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	4.00mm,Injection4	ISO 178	2400	Mpa
bending strength	3.20mm,Injection	ASTM D790	93.8	Mpa
bending strength	bending strength	4.00mm,Injection4	ISO 178	94.0	Mpa
Tensile modulus	3.20mm,Injection	ASTM D638	2210	Mpa
Tensile modulus	Tensile modulus	4.00mm,Injection	ISO 527-2/50	2200	Mpa
tensile strength	Yield,3.20mm,Injection3	ASTM D638	60.0	Mpa
	tensile strength	Yield,4.00mm,Injection	ISO 527-2/50	60.0	Mpa
		tensile strength	Break,3.20mm,Injection	ASTM D638	57.9	Mpa
		tensile strength	tensile strength	Break,4.00mm,Injection	ISO 527-2/50	58.0	Mpa
elongation	Yield,3.20mm,Injection	ASTM D638	6.2	%
	elongation	Yield,4.00mm,Injection	ISO 527-2/50	6.0	%
		elongation	Break,3.20mm,Injection	ASTM D638	110	%
		elongation	elongation	Break,4.00mm,Injection	ISO 527-2/50	110	%
Bending modulus	3.20mm,Injection	ASTM D790	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	139	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	127	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Vicat softening temperature	--	ASTM D15256	149	°C
	Vicat softening temperature	--	ISO 306/A120	150	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	144	°C
Ball pressure temperature		IEC 60335-1	>125	°C
Linear coefficient of thermal expansion	MD：-22to85°C	ASTM D696	6.5E-05	cm/cm/°C
RTI Elec		UL 746	125	°C
RTI Imp		UL 746	125	°C
RTI		UL 746	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTMD1238	10	g/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale,3.20mm,Injection	ASTM D785	123
Rockwell hardness	Rockwell hardness	R-Sale,4.00mm	ISO 2039-2	123

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.