other	Test Condition	Test Method	Test Result
notes			采用己烯作为共聚单体的中分子量高密度聚乙烯树脂。产品中添加了一定数量的PPA.具有更好的加工性能和制品表面性能.表现为产量高、能耗低、制品表面光洁度好。
purpose			主要为满足市场有更高大产量需求(如.多功位挤出机)、小容量的吹塑制品的需求而设计.适用范围为5升以下中空容器。用于盛装如食品、油和普通化学品等

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate		GB/T 3682	5 g/10min
density		ISO 1872/1-1986	0.955 g/cm

Mechanical properties	Test Method	Test Result
elongation at break	ASTM D638/ISO 527	450 %
Flexural modulus	ASTM D790/ISO 178	1200(MPa) kg/cm²(MPa)[Lb/in²]
Environmental stress cracking resistance	ASTM D-1693	50 hours
Impact strength of cantilever beam gap	ISO 179-1982	8.5 KJ/m
tensile strength	ISO R527-1966:Type2 speed D	26 Mpa
elongation	ISO R527-1966:Type2 speed D	450 %
Flexural modulus	ISO 178-1975	1200 Mpa

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	0.955

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.