Material Description

Material Properties:Middle flow｜Thermal stability
Application Areas:Lighting applications｜Plastic bag
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness	H358/30	ISO 2039-1	115 Mpa

thermal performance	Test Condition	Test Method	Test Result
vicat	--	ISO 306/B50	141 °C
vicat	vicat	--	ISO 306/B120	143 °C
ball-indentation hardness	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	4.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：23到80°C	ISO 11359-2	4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	8.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	7E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.21 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
Heat Deflection Temperature	0.45MPa,未退火,3.20mm	ASTM D648	143 °C
	Heat Deflection Temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	144 °C
		Heat Deflection Temperature	1.8MPa,未退火,3.20mm	ASTM D648	138 °C
			Heat Deflection Temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	136 °C
			Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,Annealed	ISO 75-2/Ae	136 °C
vicat		ASTM D152514	149 °C
RTI Str		UL 746	130 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825 °C
Limiting Oxygen Index		ISO 4589-2	37 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C8	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ASTM D256	80 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	110 J/m
		Impact strength of cantilever beam gap	-30°C10	ISO 180/1A	8.0 kJ/m²
			Impact strength of cantilever beam gap	-30°C11	ISO 180/1A	8.0 kJ/m²
				Impact strength of cantilever beam gap	23°C11	ISO 180/1A	10 kJ/m²
					Impact strength of cantilever beam gap	23°C10	ISO 180/1A	8.0 kJ/m²
					Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	1600 J/m
Suspended wall beam without notch impact strength	-30°C10	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C11	ISO 180/1U	130 kJ/m²
Charpy Notched Impact Strength	-30°C8	ISO 179/1eA	9.0 kJ/m²
	Charpy Notched Impact Strength	23°C9	ISO 179/1eA	9.0 kJ/m²
		Charpy Notched Impact Strength	23°C8	ISO 179/1eA	10 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/2C	15 kJ/m²
Impact strength of simply supported beam without notch	-30°C9	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C8	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C9	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	23°C11	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C10	ISO 180/1U	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	61.0 J

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.26 g/cm³
density	density		ISO 1183	1.25 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0 g/10min
Melt volume flow rate	300°C/1.2kg	ISO 1133	7.00 cm3/10min
shrinkage rate	MD：--2	内部方法	0.20-0.60 %
shrinkage rate	shrinkage rate	MD：3.20mm	内部方法	0.50-0.70 %
Water absorption rate	饱和,23°C	ISO 62	0.31 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.13 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation Factor	60Hz	IEC 60250	1E-03
Dissipation Factor	Dissipation Factor	1MHz	IEC 60250	0.010
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V
Surface Resistivity		IEC 60093	>1.0E+15 ohms
volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric strength	0.800mm,在油中	IEC 60243-1	33 KV/mm
	dielectric strength	1.60mm,在油中	IEC 60243-1	25 KV/mm
	dielectric strength	dielectric strength	3.20mm,在油中	IEC 60243-1	16 KV/mm
relative permittivity	50Hz	IEC 60250	2.90
	relative permittivity	60Hz	IEC 60250	2.90
	relative permittivity	relative permittivity	1MHz	IEC 60250	2.80
Dissipation Factor	50Hz	IEC 60250	1E-03

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	3930 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3300 Mpa
bending strength		ISO 178	95.0 Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	108 Mpa
Taber abraser	1000Cycles,1000g,CS-17转轮	内部方法	11.0 mg
tensile strength	屈服	ASTM D638	63.0 Mpa
	tensile strength	屈服	ISO 527-2/5	60.0 Mpa
		tensile strength	Break	ASTM D638	48.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/5	45.0 Mpa
elongation	屈服	ASTM D638	3.0 %
Tensile strain	屈服	ISO 527-2/5	5.0 %
elongation	断裂	ASTM D638	12 %
Tensile strain	断裂	ISO 527-2/5	7.0 %
flexural modulus	50.0mmSpan	ASTM D790	3530 Mpa
flexural modulus	flexural modulus		ISO 178	3400 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.