PBT Cristin® HR5330HF-NC010 DUPONT USA
205
- Unit Price:US$ 4,813 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:45MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Hydrolysis resistance｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Electronic and electrical components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 225 ℃ | |
| Heat Deflection Temperature | 0.45 Mpa，未退火 | ISO 75B-1 | 221 ℃ |
| 1.80 Mpa，未退火 | ISO 75B-1 | 207 ℃ | |
| Linear coefficient of thermal expansion | TD：55to160°C | ISO 11359-2 | 1.5E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 221 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 207 °C | |
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 2E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.5E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.5E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 30 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| Flammability level | 0.75mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| FMVSS flammability | FMVSS302 | B |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| 23°C | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 11 kJ/m² |
| 23°C | ISO 180/1A | 14 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 65 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.5 g/cm | |
| MediumDensity | 1.29 g/cm³ | ||
| density | ISO 1183 | 1.50 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.35 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % | |
| viscosity number | ISO 307 | 95.0 cm³/g | |
| FlowLength2 | 2.00mm，FlowLength | 350 mm | |
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 1730 J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 100Hz | IEC 60250 | 2.5E-03 |
| 1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | -- | IEC 60243-1 | 44 KV/mm |
| 1.00mm5 | IEC 60243-1 | 31 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.40 |
| 1MHz | IEC 60250 | 4.10 | |
| Dissipation Factor | 100Hz | ASTM D150 | 2.5E-03 |
| 1kHz | ASTM D150 | 7E-03 | |
| 1MHz | ASTM D150 | 0.020 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | 23℃，屈服 | ISO 527-1 | 134 MPa |
| elongation | 23℃，屈服 | ISO 527-1 | 3.5 % |
| Tensile modulus | 23℃ | ISO 527-1 | 8500 MPa |
| flexural modulus | 23℃ | ISO 178 | 7800 MPa |
| bending strength | 23℃ | ISO 178 | 203 MPa |
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | 75.1 KJ/m |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 11.5 KJ/m |
| 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 14.9 KJ/m | |
| Impact strength of cantilever beam gap | -40 ℃, Type 1, Notch A | ISO 180 | 11.1 KJ/m |
| 23 ℃, Type 1, Notch A | ISO 180 | 16.3 KJ/m | |
| tensile strength | 断裂 | ISO 527-2 | 132 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| flexural modulus | ISO 178 | 7700 Mpa | |
| bending strength | ISO 178 | 200 Mpa | |
| Poisson's ratio | ISO 527 | 0.34 | |
| Tensile modulus | ISO 527-2 | 8500 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.