PC LEXAN™ HFD4472-7N1D050 SABIC INNOVATIVE NANSHA
212
- Unit Price:US$ 5,506 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Hydrolysis resistance
- Application Areas:Electrical applications｜Automotive Applications｜Mechanical accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 10 g/10 min | |
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20 - 0.30 % | |
| 内部方法 | 0.40 - 0.50 % | ||
| Water absorption rate | ISO 62 | 0.12 % | |
| ISO 62 | 0.040 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 5500 Mpa | |
| tensile strength | ASTM D638 | 54.0 Mpa | |
| ISO 527-2/5 | 54.0 Mpa | ||
| ASTM D638 | 56.0 Mpa | ||
| ISO 527-2/5 | 56.0 Mpa | ||
| elongation | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 2.0 % | ||
| Flexural modulus | ASTM D790 | 4900 Mpa | |
| bending strength | ASTM D790 | 93.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 13 kJ/m² | |
| ISO 179/1eA | 21 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 59 kJ/m² | |
| ISO 179/1eU | 59 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D4812 | 800 J/m | |
| ISO 180/1U | 43 kJ/m² | ||
| ISO 180/1U | 47 kJ/m² | ||
| Dart impact | ASTM D3763 | 30.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 内部方法 | 3.16 | |
| Dissipation Factor | 内部方法 | 9.9E-3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 265 to 290 °C | ||
| Temperature in the middle of the barrel | 275 to 300 °C | ||
| Temperature at the front of the material cylinder | 290 to 310 °C | ||
| Spray nozzle temperature | 280 to 305 °C | ||
| Processing (melt) temperature | 290 to 310 °C | ||
| Temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 132 °C | |
| ASTM D648 | 128 °C | ||
| vicat | ISO 306/B120 | 135 °C | |
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 3.0E-5 cm/cm/°C | |
| ISO 11359-2 | 3.0E-5 cm/cm/°C | ||
| ASTM E831 | 8.0E-5 cm/cm/°C | ||
| ISO 11359-2 | 8.0E-5 cm/cm/°C | ||
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.