PC LEXAN™ 104R-111 SABIC INNOVATIVE NANSHA
193
- Unit Price:US$ 2,019 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:Food packaging｜Nursing supplies｜Medical supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 | |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.7E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1250 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| ISO 8302 | 0.20 W/m/K | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,100mm跨距10 | ISO 75-2/Ae | 127 °C |
| 1.8MPa,未退火,64.0mm跨距11 | ISO 75-2/Af | 124 °C | |
| vicat | ASTM D152512 | 154 °C | |
| -- | ISO 306/B50 | 144 °C | |
| -- | ISO 306/B120 | 145 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| 140°C13 | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.2E-05 cm/cm/°C |
| MD：-40to40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 137 °C |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 138 °C | |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 132 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| ISO 489 | 1.586 | ||
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| 23°C | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 630 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| 60Hz | ASTM D150 | 3.17 | |
| 1MHz | ASTM D150 | 2.96 | |
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| 60Hz | IEC 60250 | 2.70 | |
| 1MHz | IEC 60250 | 2.70 | |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| 60Hz | ASTM D150 | 9E-04 | |
| 1MHz | ASTM D150 | 0.010 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 4.00 cm3/10min |
| 300°C/1.2kg | ISO 1133 | 6.00 cm3/10min | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| 平衡,100°C | ASTM D570 | 0.58 % | |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂 | ASTM D638 | 68.0 Mpa | |
| 断裂 | ISO 527-2/50 | 70.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 140 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| ISO 178 | 2300 Mpa | ||
| bending strength | ISO 178 | 90.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 97.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTM D1044 | 10.0 mg |
| 1000Cycles,1000g,CS-17Wheel | 内部方法 | 10.0 mg | |
| Tensile modulus | ASTM D638 | 2310 Mpa | |
| ISO 527-2/1 | 2350 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.