PBT VALOX™ VX5022-7001 SABIC INNOVATIVE US
198
- Unit Price:US$ 3,492 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High crystallinity｜Aging resistance｜Filler: Glass fiber reinforced material｜20% filler by weight
- Application Areas:engineering application ｜Automotive components｜Electronic and electrical components
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 122 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 205 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 1E-04 cm/cm/°C |
| 横向, -40到40℃ | ISO 11359-2 | 6.9E-05 cm/cm/°C | |
| Horizontal: 23 to 60 ° C | 横向, 23到60℃ | ISO 11359-2 | 1E-04 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 1E-04 cm/cm/°C |
| Horizontal: 23 to 150 ° C | 横向, 23到150℃ | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 120 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 120 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Flow: -40 to 40 ° C | ASTME831 | 4E-05 cm/cm/°C | |
| ISO 11359-2 | 2.5E-05 cm/cm/°C | ||
| Flow: 23 to 60 ° C | 23到60℃ | ISO 11359-2 | 4E-05 cm/cm/°C |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 4E-05 cm/cm/°C |
| Flow: 23 to 150 ° C | 23到150℃ | ISO 11359-2 | 2.4E-05 cm/cm/°C |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 180 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 180 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 750 °C |
| 2.00mm | IEC 60695-2-12 | 850 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 23 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 20 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 215 Pa·s |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| -30°C | ISO 179/1eA | 5.5 kJ/m² | |
| ISO 179/2C | 9.0 kJ/m² | ||
| 23°C | ISO 179/1eA | 6.5 kJ/m² | |
| ISO 179/2C | 9.0 kJ/m² | ||
| -30°C | ISO 179/1eU | 40 kJ/m² | |
| ISO 179/2U | 50 kJ/m² | ||
| 23°C | ISO 179/1eU | 40 kJ/m² | |
| ISO 179/2U | 55 kJ/m² | ||
| -30°C | ASTM D256 | 80 J/m | |
| 0°C | ASTM D256 | 80 J/m | |
| 23°C | ASTM D256 | 80 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| 23°C | ISO 180/1U | 40 kJ/m² | |
| -30°C | ISO 180/1U | 35 kJ/m² | |
| 23°C | ASTM D4812 | 650 J/m | |
| ISO 180/1A | 7.0 kJ/m² | ||
| -30°C | ASTM D4812 | 650 J/m | |
| 0°C | ISO 180/1A | 7.0 kJ/m² | |
| -30°C | ISO 180/1A | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50Hz | 50Hz | IEC 60250 | 1E-03 |
| 1MHz | 1MHz | ASTMD150 | 0.014 |
| 100Hz | 100Hz | IEC 60250 | 3.30 |
| 60Hz | 60Hz | IEC 60250 | 3.10 |
| 60Hz | IEC 60250 | 1E-03 | |
| 100Hz | 100Hz | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 3 |
| 解决方案B | IEC 60112 | PLC 4 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| 0.800mm, inoil | ASTM D149 | 31 KV/mm | |
| 16mm, inoyl | ASTM D149 | 28 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 16 KV/mm | |
| 50Hz | 50Hz | IEC 60250 | 3.10 |
| 3.20mm, In oil | IEC 60243-1 | 16 KV/mm | |
| 1MHz | 1MHz | ASTMD150 | 3.30 |
| 1.60mm, In oil | IEC 60243-1 | 28 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 31 KV/mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.10 % |
| 平衡,23°C,50%RH | ISO 62 | 0.060 % | |
| shrinkage rate | TD2 | 内部方法 | 0.50-0.90 % |
| MD:3.20mm | 内部方法 | 0.30-0.50 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 40.0 cm3/10min |
| shrinkage rate | MD1 | 内部方法 | 0.30-0.80 % |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 50 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 28.0 cm3/10min |
| 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min | |
| density | ASTMD792 | 1.39 g/cm³ | |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 16 g/10min |
| 265°C/5.0kg | ASTM D1238 | 50 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| yield | ASTM D638 | 3.0 % | |
| ISO 527-2/5 | 3.0 % | ||
| fracture | ASTM D638 | 3.0 % | |
| ISO 527-2/5 | 3.0 % | ||
| 50.0mm span | ASTM D790 | 5800 Mpa | |
| --9 | ISO 178 | 6300 Mpa | |
| --10 | ISO 178 | 150 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 145 Mpa | |
| Fracture bending strain | ISO 178 | 3.0 % | |
| --3 | ASTM D638 | 7300 Mpa | |
| yield | ASTM D638 | 125 Mpa | |
| ISO 527-2/5 | 110 Mpa | ||
| fracture | ASTM D638 | 125 Mpa | |
| ISO 527-2/5 | 110 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.