Material Description

Material Properties:Dimensional stability｜Low viscosity｜Aging resistance｜heat-resisting｜Antichemical｜Glass fiber reinforced
Application Areas:--
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	520 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.30 mm	UL 94	V-0
Extreme Oxygen Index		ISO 527-1	48 %
Solder resistance		Internal Method	330 °C

mechanical properties	Test Condition	Test Method	Test Result
Poisson's ratio		ASTM D785	0.49
shear strength		ASTM D732	52.0 Mpa
bending strength	200°C	ASTM D790	39.0 Mpa
bending strength	bending strength	23°C	ASTM D790	139 Mpa
Bending modulus	200°C	ASTM D790	6300 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	12300 Mpa
elongation	Break	ASTM D638	5.0 %
tensile strength		ASTM D638	150 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			130 °C
drying time			4.0 to 24 hr
Temperature at the rear of the barrel			330 to 350 °C
Temperature in the middle of the barrel			350 to 370 °C
Temperature at the front of the material cylinder			370 to 390 °C
Spray nozzle temperature			370 to 390 °C
Processing (melt) temperature			380 °C
Mold temperature			40 to 160 °C
Injection pressure			120 to 160 Mpa
Injection speed			中等偏快
Maintain pressure			40.0 to 60.0 Mpa
Back pressure			1.00 to 5.00 Mpa
Screw speed			50 to 100 rpm

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		JIS R2618	0.57 W/m/K
Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	6.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 150°C	Internal Method	1.4E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	313 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation	ASTM D570	0.020 %
Shrinkage rate	Flow	Internal Method	0.10 %
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 4
Arc resistance		ASTM D495	130 sec
Dissipation factor	1 MHz	ASTM D150	0.034
Dissipation factor	Dissipation factor	1 kHz	ASTM D150	0.018
Dielectric constant	1 MHz	ASTM D150	3.90
Dielectric constant	Dielectric constant	1 kHz	ASTM D150	4.50
Volume resistivity		ASTM D257	1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	91

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP SUMIKASUPER® E4008 MR SUMITOMO JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet