Plastic Raw Materials
PBT/PC

PBT/PC XENOY™  5220U SABIC INNOVATIVE SHANGHAI

372
  • Unit Price:US$ 3,494 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    153MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Antichemical｜Low temperature impact resistance
  • Application Areas:chip｜Household goods｜Electrical appliances｜sporting goods｜Plastic bag｜Automotive External Parts｜Lighting applications
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C, Total EnergyASTM D376360.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--3ASTM D6382250 Mpa
Tensile modulus--4ASTM D6382250 Mpa
Tensile modulus--ISO 527-2/12050 Mpa
tensile strengthYield5ASTM D63853.0 Mpa
tensile strengthYieldISO 527-2/5050.0 Mpa
tensile strengthBreak5ASTM D63851.0 Mpa
tensile strengthBreakISO 527-2/5050.0 Mpa
elongationYield5ASTM D6384.0 %
elongationYieldISO 527-2/504.0 %
elongationBreak5ASTM D638120 %
elongationBreakISO 527-2/50120 %
Bending modulus50.0 mm Span6ASTM D7902030 Mpa
Bending modulus--7ISO 1782000 Mpa
bending strength--7,8ISO 17880.0 Mpa
bending strengthYield, 50.0 mm Span6ASTM D79084.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature110 °C
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume50 to 80 %
Temperature at the rear of the barrel245 to 265 °C
Temperature in the middle of the barrel250 to 270 °C
Temperature at the front of the material cylinder255 to 275 °C
Spray nozzle temperature255 to 270 °C
Processing (melt) temperature260 to 275 °C
Mold temperature65 to 90 °C
Back pressure0.300 to 0.700 Mpa
Screw speed50 to 80 rpm
Exhaust hole depth0.013 to 0.020 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648107 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64884.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D64899.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10ISO 75-2/Af75.0 °C
Vicat softening temperature--ASTM D152511122 °C
Vicat softening temperature--ISO 306/B50120 °C
Vicat softening temperature--ISO 306/B120125 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8319.5E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8319.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-29.0E-5 cm/cm/°C
RTI ElecUL 74675.0 °C
RTI ImpUL 74675.0 °C
RTIUL 74675.0 °C
Physical propertiesTest ConditionTest MethodTest Result
Specific volumeASTM D7920.830 cm³/g
melt mass-flow rate250°C/5.0 kgISO 113316 g/10 min
Melt Volume Flow Rate (MVR)250°C/5.0 kgISO 113315.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.80 - 1.0 %
Shrinkage rateAcross FlowFlow 2Internal Method0.80 - 1.0 %
Water absorption rateSaturation, 23°CISO 620.50 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Outdoor applicabilityUL 746Cf2
Electrical performanceTest ConditionTest MethodTest Result
Arc resistanceASTM D495PLC 5
Compared to the anti leakage trace indexUL 746PLC 1
High arc combustion indexUL 746PLC 0
High voltage arc tracing rateUL 746PLC 0
Hot wire ignitionUL 746PLC 3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.