PA6

PA6 Amilan® CM1001R TORAY JAPAN

218

Unit Price:US$ 3,299 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
84MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 0.75mm
	UL flame retardant rating		UL -94	HB 1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	95 Mpa
tensile strength	tensile strength	-40°C	ISO 527-2	130 Mpa
Elongation at Break	23°C	ISO 527-2	2.5 %
Elongation at Break	Elongation at Break	-40°C	ISO 527-2	2.0 %
bending strength	23°C	ISO 178	145 Mpa
bending strength	bending strength	-40°C	ISO 178	160 Mpa
Bending modulus	23°C	ISO 178	5800 Mpa
Bending modulus	Bending modulus	-40°C	ISO 178	6900 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-40°C	ISO 179/1eU	35 kJ/m²
Rockwell hardness		ASTM D785	R119.M81

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	203 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	173 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05 cm/cm/°C
Melting temperature			225 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	(23°C,24hr)	ISO 62	0.90 %
density		ASTM D792/ISO 1183	1.51
Water absorption rate		ASTM D570/ISO 62	0.9 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	23°C	IEC 60250	4.5 1kHz
Dielectric constant	Dielectric constant	23°C	IEC 60250	3.8 1MHz
Dissipation factor	23°C	IEC 60250	0.03 1kHz
Dissipation factor	Dissipation factor	23°C	IEC 60250	0.02 1MHz
Volume resistivity		IEC 60093	1E+15 Ω.cm
Dielectric strength	3.00mm	IEC 60243-1	21 KV/mm
Volume resistivity		ASTM D257/IEC 60093	10^13 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	81 M（Scale）
Rockwell hardness	Rockwell hardness		ISO 2039-2	119 R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Amilan® CM1001R TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet