PA66

PA66 LNP™ LUBRICOMP™ RAL23S-YWLTNAT SABIC INNOVATIVE US

122

Unit Price:US$ 6,441 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance
Application Areas:Home appliance components
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	37 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	3680 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3800 Mpa
tensile strength	Break	ASTM D638	89.6 Mpa
tensile strength	tensile strength	Break	ISO 527-2	85.0 Mpa
elongation	Break	ASTM D638	5.9 %
Tensile strain	Break	ISO 527-2	6.3 %
Bending modulus		ASTM D790	3940 Mpa
Bending modulus	Bending modulus		ISO 178	3500 Mpa
bending strength		ASTM D790	131 Mpa
bending strength	bending strength		ISO 178	107 Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.38
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.32
Wear factor	Washer	ASTM D3702Modified	23.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ASTM D638	3680 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3800 Mpa
Bending modulus		ASTM D790	3940 Mpa
Bending modulus	Bending modulus		ISO 178	3500 Mpa
bending strength		ASTM D790	131 Mpa
bending strength	bending strength		ISO 178	107 Mpa
Wear factor	Washer	ASTM D3702Modified	23.0 10^-10in^5-min/ft-lb-hr

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	246 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	171 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	160 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	9.7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	9.8E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	1.7-1.8 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	2.0-2.1 %
density		ISO 1183	1.23 g/cm³
density	density		ASTM D792	1.24 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 LNP™ LUBRICOMP™ RAL23S-YWLTNAT SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet