Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NoBreak
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
NoBreak
flammability
Test Condition
Test Method
Test Result
FMVSS flammability
FMVSS302
B
Extreme Oxygen Index
ISO 4589-2
25 %
UL flame retardant rating
1.5mm
IEC 60695-11-10,-20
HB
UL flame retardant rating
0.9mm
IEC 60695-11-10,-20
HB
Burning rate
1.00mm
ISO 3795
<100 mm/min
UL flame retardant rating
0.9mm
UL 94
HB
UL flame retardant rating
1.5mm
UL 94
HB
mechanical properties
Test Condition
Test Method
Test Result
Nominal tensile fracture strain
ISO 527-2
35 %
Tensile strain
Yield
ISO 527-2
4.3 %
tensile strength
Yield
ISO 527-2
62.0 Mpa
Tensile modulus
ISO 527-2
2400 Mpa
Charpy Notched Impact Strength
ASTM D256/ISO 179
4 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength
ASTM D256/ISO 179
NB kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength
ASTM D256/ISO 179
5 kg·cm/cm(J/M)ft·lb/in
Elongation at Break
ASTM D412/ISO 527
35 %
Tensile modulus
ASTM D412/ISO 527
2050 kg/cm²(MPa)[Lb/in²]
tensile strength
ASTM D412/ISO 527
62 kg/cm²(MPa)[Lb/in²]
thermal performance
Test Condition
Test Method
Test Result
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.2E-04 cm/cm/°C
Melting temperature
ISO 11357-3
218 °C
Vicat softening temperature
ISO 306/B50
180 °C
Glass transition temperature
ISO 11357-2
60.0 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
62.0 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
135 °C
Linear coefficient of thermal expansion
TD
ISO 11359-2
1.2E-04 cm/cm/°C
Combustibility (rate)
UL 94
HB
Hot deformation temperature
HDT
ASTM D648/ISO 75
135 ℃（℉）
Hot deformation temperature
HDT
ASTM D648/ISO 75
62 ℃（℉）
Melting temperature
218 ℃（℉）
Linear coefficient of thermal expansion
ASTM D696/ISO 11359
0.9-1.8
Physical properties
Test Condition
Test Method
Test Result
Shrinkage rate
TD：3.20mm
1.1 %
Shrinkage rate
TD
ISO 294-4
1.5 %
Shrinkage rate
MD
ISO 294-4
1.5 %
Shrinkage rate
MD：3.20mm
1.1 %
SpecificHeatCapacity of Melt
2800 J/kg/°C
MediumDensity
0.900 g/cm³
Stickiness
96%H2SO4
ISO 307
120 cm³/g
ThermalConductivityofMelt
0.19 W/m/K
Water absorption rate
Saturation,23°C,2.00mm
ISO 62
3.0 %
Water absorption rate
Equilibrium,23°C,2.00mm,50%RH
ISO 62
1.3 %
Shrinkage rate
ASTM D955
1.3-1.4 %
density
ASTM D792/ISO 1183
1.06
Water absorption rate
ASTM D570/ISO 62
1.3 %
Electrical performance
Test Condition
Test Method
Test Result
Surface resistivity
IEC 60093
-- ohms
Volume resistivity
IEC 60093
>1.0E+15 ohms·cm
Dielectric strength
IEC 60243-1
36 KV/mm
Relative permittivity
100Hz
IEC 60250
3.60
Relative permittivity
1MHz
IEC 60250
3.20
Dissipation factor
100Hz
IEC 60250
0.014
Dissipation factor
1MHz
IEC 60250
0.017
hardness
Test Condition
Test Method
Test Result
Rockwell hardness
R-Scale
ISO 2039-2
114
film
Test Condition
Test Method
Test Result
Tensile strain
Yield，MD
ISO 527-3
4.3 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)