PPO/PA

PPO/PA NORYL GTX™  GTX918WR-7001 SABIC INNOVATIVE JAPAN

392
  • Unit Price:US$ 4,717 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    45MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Aging resistance｜High temperature resistance
  • Application Areas:household electrical appliances｜Electronic communication｜Automotive interior parts
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA10 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA20 kJ/m²
Dart impact23°C, Energy at PeakASTM D376340.0 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D638810 Mpa
tensile strengthYield3ASTM D63862.0 Mpa
tensile strengthYieldISO 527-2/5060.0 Mpa
tensile strengthBreak3ASTM D63857.0 Mpa
tensile strengthBreakISO 527-2/5055.0 Mpa
elongationYield3ASTM D63811 %
elongationYieldISO 527-2/504.5 %
elongationBreak3ASTM D63853 %
elongationBreakISO 527-2/5030 %
Bending modulus50.0 mm Span4ASTM D7902360 Mpa
Bending modulus--5ISO 1782200 Mpa
bending strength--5,6ISO 17885.0 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79098.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature95 to 105 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.070 %
Suggested injection volume30 to 50 %
Temperature at the rear of the barrel255 to 295 °C
Temperature in the middle of the barrel260 to 295 °C
Temperature at the front of the material cylinder265 to 295 °C
Spray nozzle temperature270 to 295 °C
Processing (melt) temperature270 to 295 °C
Mold temperature65 to 95 °C
Back pressure0.300 to 1.40 Mpa
Screw speed20 to 100 rpm
Exhaust hole depth0.013 to 0.038 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648188 °C
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Be185 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648148 °C
Vicat softening temperature--ASTM D152510242 °C
Vicat softening temperature--ISO 306/A50245 °C
Vicat softening temperature--ISO 306/B50190 °C
Vicat softening temperature--ISO 306/B120195 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8316.5E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 60°CISO 11359-28.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.8E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 60°CISO 11359-28.0E-5 cm/cm/°C
thermal conductivityASTM C1770.25 W/m/K
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate280°C/5.0 kgASTM D123845 g/10 min
Melt Volume Flow Rate (MVR)280°C/1.2 kgISO 11335.00 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method1.3 - 1.6 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method1.0 - 1.3 %
Water absorption rateSaturation, 23°CASTM D5704.2 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.