LCP VECTRA® B230 BK CELANESE USA
186
- Unit Price:US$ 6,249 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Conductive｜High rigidity｜high strength｜Halogen-free｜Flame retardant｜Carbon fiber reinforced
- Application Areas:Metal substitution
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 99 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 250 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 235 °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 186 °C | |
| vicat | ISO 306/B50 | 167 °C | |
| melting temperature | ISO 11357-3 | 280 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 9.0E-6 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 12 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 0.10 % |
| 流量 | ISO 294-4 | 0.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+2 ohms | |
| volume resistivity | IEC 60093 | 1.0E+5 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 32.0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 °C | ||
| drying time | 6.0 to 8.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Hopper temperature | 20 to 30 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Spray nozzle temperature | 290 to 300 °C | ||
| Processing (melt) temperature | 285 to 300 °C | ||
| mold temperature | 80 to 120 °C | ||
| injection speed | 快速 | ||
| Back pressure | < 3.00 Mpa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 31800 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 200 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 0.70 % |
| flexural modulus | 23°C | ISO 178 | 25500 Mpa |
| bending strength | 23°C | ISO 178 | 300 Mpa |
| Compression Modulus | ISO 604 | 33000 Mpa | |
| compression stress | 1% 应变 | ISO 604 | 204 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.