PBT

PBT VALOX™ 508-1001 SABIC INNOVATIVE SHANGHAI

260

Unit Price:US$ 4,168 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage｜Glass fiber reinforced
Application Areas:Laptop case｜Phone case｜Home appliance components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	8.00 J
Dart impact	Dart impact	23°C, Energy at Peak	ASTM D3763	6.00 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	640 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break, 50.0 mm Span	ASTM D790	189 Mpa
Bending modulus	50.0 mm Span	ASTM D790	6890 Mpa
tensile strength	Break	ASTM D638	110 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 80 %
Temperature at the rear of the barrel			240 to 255 °C
Temperature in the middle of the barrel			245 to 260 °C
Temperature at the front of the material cylinder			250 to 265 °C
Spray nozzle temperature			245 to 260 °C
Processing (melt) temperature			250 to 265 °C
Mold temperature			65 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			50 to 80 rpm
Exhaust hole depth			0.025 to 0.038 mm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	125 °C
RTI Imp		UL 746	110 °C
RTI Elec		UL 746	125 °C
Linear coefficient of thermal expansion	60 to 138°C，Flow	ASTM E831	1.6E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	-40 to 40°C，Flow	ASTM E831	2.3E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	176 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	215 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f2
Water absorption rate	24 hr	ASTM D570	0.060 %
Shrinkage rate	Across FlowFlow : 3.20 to 4.60 mm	Internal Method	0.60 - 0.90 %
	Shrinkage rate	Across FlowFlow : 1.50 to 3.20 mm	Internal Method	0.40 - 0.60 %
		Shrinkage rate	Flow : 3.20 to 4.60 mm	Internal Method	0.50 - 0.80 %
		Shrinkage rate	Shrinkage rate	Flow : 1.50 to 3.20 mm	Internal Method	0.30 - 0.50 %
Specific volume		ASTM D792	0.660 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	100 Hz	ASTM D150	3.60
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.60
Dielectric strength	3.20 mm, in Air	ASTM D149	24 KV/mm
Dielectric strength	Dielectric strength	1.60 mm, in Oil	ASTM D149	29 KV/mm
Volume resistivity		ASTM D257	5.9E+16 ohms·cm
Dissipation factor	100 Hz	ASTM D150	1.4E-3
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.020
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 4
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 1

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ 508-1001 SABIC INNOVATIVE SHANGHAI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet