mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ASTM D638	>150	%
Tensile strain	Break	ISO 527-2	120	%
Bending modulus		ASTM D790	2500	Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	5.1	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	120	%
tensile strength		ASTM D638/ISO 527	58	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2.4	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	83	kg/cm²(MPa)[Lb/in²]
tensile strength		ISO 527-2	58.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	54.0	Mpa
bending strength		ISO 178	83.0	Mpa
bending strength	bending strength		ASTM D790	82.0	Mpa
Bending modulus		ISO 178	2400	Mpa
Charpy Notched Impact Strength		ISO 179/1eA	5.1	KJ/m
Bending modulus		ISO 178	2.4	Gpa
bending strength		ISO 178	83	MPa
tensile strength		ISO 527-1/-2	58	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature			224	°C
UL flame retardant rating		UL94	HB
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.315
melt mass-flow rate		ASTM D1238/ISO 1133	224	g/10min
Viscosity value	0.5%OCP	Internal Method	1.23	cm³/g
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	16.0	cm3/10min
melt mass-flow rate	250°C/1.0kg	ISO 1133	8.7	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.